3M Dyneon™ THV™ 200G Fluorothermoplastic, Pellet Form  (discontinued **)

Category Polymer , Thermoplastic , Fluoropolymer
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF 3M Dyneon™ THV™ 200G Fluorothermoplastic, Pellet Form  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Dyneon LLC.This unique, melt-processable, tetrafluoroethylene, hexafluoropropylene, and vinylidene fluoride (THV) terpolymer provides a unique combination of performance and processing advantages. Its thermal decomposition in air (TGA) is 420°C. It is recommended for film, tube, and profile extrusion, wire coating, and blow and injection molding.
Physical Properties Metric English Comments
Density 1.95 g/cc
0.0704 lb/in³
Melt Flow 20 g/10 min

@Load 5.00 kg,
Temperature 260 °C
20 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 44
44
ASTM D2240
Tensile Strength, Ultimate 24.1 MPa
3500 psi
Measured on extruded film, ASTM D638
Elongation at Break 600 %
600 %
Measured on extruded film, ASTM D638
Flexural Modulus 0.0830 GPa
12.0 ksi
ASTM D790
Thermal Properties Metric English Comments
Melting Point 115 - 257 °C
239 - 495 °F
ASTM D3418
Maximum Service Temperature, Air >= 150 °C
>= 302 °F
E-beam cured high temperature resistance.
Electrical Properties Metric English Comments
Dielectric Constant 4.6

@Frequency 1e+7 Hz
4.6

@Frequency 1e+7 Hz
6.6

@Frequency 100000 Hz
6.6

@Frequency 100000 Hz
Copyright © lookpolymers.com All Rights Reserved