- Solvay Specialty Polymers AvaSpire® AV-722 CF30 Polyaryletherketone (PAEK), 30% Carbon Fiber
Solvay Specialty Polymers AvaSpire® AV-722 CF30 Polyaryletherketone (PAEK), 30% Carbon Fiber
| Category | Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Carbon Fiber Filled |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | AvaSpire® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers AvaSpire® AV-722 CF30 Polyaryletherketone (PAEK), 30% Carbon Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AvaSpire® AV-722 CF30 is a 30% carbon fiber reinforced version of AvaSpire® AV-722. This formulation offers improved part economics relative to 30% carbon fiber reinforced PEEK while retaining most of the desirable high performance attributes of carbon fiber reinforced PEEK. Those attributes include chemical resistance, fatigue resistance, and long term thermal oxidative stability.Features: Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; High Heat Resistance; High Stiffness; High StrengthUses: Automotive Applications; Gears; Industrial ApplicationsInjection Molding Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 |
| Filler Content | 30 % | 30 % | Carbon Fiber |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ISO 62 |
| Viscosity | 470000 cP @Shear Rate 1000 1/s, Temperature 400 °C |
470000 cP @Shear Rate 1000 1/s, Temperature 752 °F |
Melt Viscosity; ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.00 - 0.0020 cm/cm @Thickness 3.18 mm |
0.00 - 0.0020 in/in @Thickness 0.125 in |
|
| Linear Mold Shrinkage, Transverse | 0.014 - 0.016 cm/cm @Thickness 3.18 mm |
0.014 - 0.016 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 400 °C |
0.80 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 107 | 107 | ASTM D785 |
| Tensile Strength | 200 MPa | 29000 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 224 MPa | 32500 psi | 5 mm/min, Type 1A; ISO 527-2 |
| Elongation at Break | 1.5 % | 1.5 % | Type 1A, 5 mm/min; ISO 527-2 |
| 1.5 % | 1.5 % | 5 mm/min; ASTM D638 | |
| Tensile Modulus | 22.0 GPa | 3190 ksi | 5 mm/min; ASTM D638 |
| 26.6 GPa | 3860 ksi | 1 mm/min, Type 1A; ISO 527-2 | |
| Flexural Strength | 304 MPa | 44100 psi | ASTM D790 |
| 334 MPa | 48400 psi | ISO 178 | |
| Flexural Modulus | 19.3 GPa | 2800 ksi | ASTM D790 |
| 25.0 GPa | 3630 ksi | ISO 178 | |
| Compressive Strength | 170 MPa | 24700 psi | ASTM D695 |
| Poissons Ratio | 0.44 | 0.44 | ASTM E132 |
| Shear Strength | 98.0 MPa | 14200 psi | ASTM D732 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.30 J/cm | 9.93 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 8.50 kJ/m² | 4.04 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 39.0 kJ/m² | 18.6 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 6.00 µm/m-°C @Temperature -50.0 - 50.0 °C |
3.33 µin/in-°F @Temperature -58.0 - 122 °F |
1 |
| Specific Heat Capacity | 1.28 J/g-°C @Temperature 50.0 °C |
0.306 BTU/lb-°F @Temperature 122 °F |
ASTM C351 |
| 1.74 J/g-°C @Temperature 200 °C |
0.416 BTU/lb-°F @Temperature 392 °F |
ASTM C351 | |
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 340 °C | 644 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 276 °C | 529 °F | Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 150 °C | 302 °F | DSC |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 366 °C | 691 °F | |
| Middle Barrel Temperature | 371 °C | 700 °F | |
| Front Barrel Temperature | 377 °C | 711 °F | |
| Nozzle Temperature | 382 °C | 720 °F | |
| Mold Temperature | 177 - 204 °C | 351 - 399 °F | |
| Drying Temperature | 149 °C @Time 14400 sec |
300 °F @Time 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black | |
| Form | Pellets | |
| Injection Rate | Fast | |
| Processing Technique | Injection Molding; Machining; Profile Extrusion | |
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 |
Users viewing this material also viewed the following:
- Precision Polymer Engineering E50Q Ethylene Propylene Rubber
- Inno-Comp INNOPOL® CS 2-9000 Polypropylene Block-Copolymer
- SABIC Innovative Plastics LNP Verton RV008ESV PA 66
- Dow Corning 700 INDUSTRIAL GRADE SILICONE SEALANT
- DuPont Performance Polymers Zytel® 8018HS BKB085 Nylon 66 (Unverified Data**)
- Chosun Refractories N4-1 Fireclay brick
- Fainplast Compounds PM 8725 Flexible PVC, Lead Free
- Arlon CP-RC-3918 Silicone Bulk Compound
- BASF Ultramid® 8350 HS PA6 (Dry)
- Ascend Performance Materials Vydyne® R633 Nylon 66 Copolymer, 33% Glass Filled, Conditioned (2.5% Moisture)
Copyright © lookpolymers.com All Rights Reserved