Solvay Specialty Polymers Amodel® AT-6115 HS Polyphthalamide (PPA) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 20% Glass Fiber Reinforced
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers Amodel® AT-6115 HS Polyphthalamide (PPA) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amodel AT-6115 HS is a 15% glass-fiber reinforced, toughened grade of polyphthalamide (PPA) resin designed to possess more elongation than other 15% glass-fiber reinforced grades of Amodel resin. This grade was developed for automotive snap-fit electronic connectors. It offers high flow and short molding cycles. - Black: AT-6115 HS BK 324 - Natural: AT-6115 HS NTInjection Notes: Injection Rate: 2 to 4 in/sec Holding Pressure: 50% of injection pressureData is presented for dry polymer unless noted as 'conditioned'.Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.22 g/cc	0.0441 lb/in³	ISO 1183/A
Filler Content	15 %	15 %	Glass Fiber Reinforcement
Water Absorption	0.20 % @Time 86400 sec	0.20 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.010 cm/cm	0.010 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.011 cm/cm	0.011 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	68.3 MPa @Temperature 100 °C	9910 psi @Temperature 212 °F	ISO 527-2
	114 MPa @Temperature 23.0 °C	16500 psi @Temperature 73.4 °F	ISO 527-2
Tensile Strength	95.8 MPa	13900 psi	Conditioned; ASTM D638
	122 MPa	17700 psi	ASTM D638
Elongation at Break	3.4 %	3.4 %	ASTM D638
	5.3 %	5.3 %	Conditioned; ASTM D638
	3.9 % @Temperature 23.0 °C	3.9 % @Temperature 73.4 °F	ISO 527-2
	7.7 % @Temperature 100 °C	7.7 % @Temperature 212 °F	ISO 527-2
Tensile Modulus	5.38 GPa	780 ksi	ASTM D638
	6.69 GPa	970 ksi	Conditioned; ASTM D638
	3.10 GPa @Temperature 100 °C	450 ksi @Temperature 212 °F	ISO 527-2
	5.38 GPa @Temperature 23.0 °C	780 ksi @Temperature 73.4 °F	ISO 527-2
Flexural Strength	115 MPa	16700 psi	Conditioned; ASTM D790
	165 MPa	23900 psi	ASTM D790
	66.9 MPa @Temperature 100 °C	9700 psi @Temperature 212 °F	ISO 178
	170 MPa @Temperature 23.0 °C	24700 psi @Temperature 73.4 °F	ISO 178
Flexural Modulus	3.45 GPa	500 ksi	Conditioned; ASTM D790
	4.41 GPa	640 ksi	ASTM D790
	2.34 GPa @Temperature 100 °C	339 ksi @Temperature 212 °F	ISO 178
	4.27 GPa @Temperature 23.0 °C	619 ksi @Temperature 73.4 °F	ISO 178
Compressive Strength	100 MPa	14500 psi	ASTM D695
Shear Strength	44.1 MPa	6400 psi	Conditioned; ASTM D732
	56.5 MPa	8190 psi	ASTM D732
Izod Impact, Notched	0.800 J/cm	1.50 ft-lb/in	Conditioned; ASTM D256
	0.910 J/cm	1.70 ft-lb/in	ASTM D256
	8.50 J/cm	15.9 ft-lb/in	ASTM D256
Izod Impact, Notched (ISO)	12.0 kJ/m²	5.71 ft-lb/in²	ISO 180/1A
Izod Impact, Unnotched (ISO)	55.0 kJ/m² @Temperature 23.0 °C	26.2 ft-lb/in² @Temperature 73.4 °F	ISO 180/1U
Charpy Impact Unnotched	7.60 J/cm²	36.2 ft-lb/in²	ISO 179/1eU
Charpy Impact, Notched	1.10 J/cm²	5.23 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	22.0 µm/m-°C @Temperature 0.000 - 100 °C	12.2 µin/in-°F @Temperature 32.0 - 212 °F	TMA; ASTM E831
	30.0 µm/m-°C @Temperature 100 - 200 °C	16.7 µin/in-°F @Temperature 212 - 392 °F	TMA; ASTM E831
CTE, linear, Transverse to Flow	90.0 µm/m-°C @Temperature 0.000 - 100 °C	50.0 µin/in-°F @Temperature 32.0 - 212 °F	ASTM E831
	120 µm/m-°C @Temperature 100 - 200 °C	66.7 µin/in-°F @Temperature 212 - 392 °F	ASTM E831
Melting Point	307 °C	585 °F	Peak; ASTM D3418
	307 °C	585 °F	ISO 11357-3
Deflection Temperature at 0.46 MPa (66 psi)	298 °C	568 °F	Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi)	265 °C	509 °F	Unannealed; ISO 75-2/A
	271 °C	520 °F	Annealed; ASTM D648

Processing Properties	Metric	English
Rear Barrel Temperature	316 - 324 °C	601 - 615 °F
Front Barrel Temperature	327 - 332 °C	621 - 630 °F
Melt Temperature	321 - 335 °C	610 - 635 °F
Mold Temperature	65.6 - 93.3 °C	150 - 200 °F
Drying Temperature	110 °C	230 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	0.045 %	0.045 %

Descriptive Properties	Value	Comments
Additive	Heat Stabilizer
	Impact Modifier
	Lubricant
	Mold Release
Appearance	Black
	Natural Color
Automotive Specifications	ASTM D4000 PA103 G15
	ASTM D4000 PPA0123 G15 GB121 KD100 KN042 PN068 YI242
	ASTM D6779 PA103G15
	DELPHI M-4628 Color: BK324 Black
	DELPHI M-4628 Color: NT Natural
	FORD WSS-M4D943-A2 Color: BK324 Black
	FORD WSS-M4D943-A2 Color: NT Natural
	GM GMP.PPA.020 Color: BK-324, NT Black & Natural
	ISO 1874 PA6T/66-HI, MH, 11-050, GF15
Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Features	Fast Molding Cycle
	Good Mold Release
	Heat Stabilized
	High Elongation
	High Flow
	Impact Modified
	Lubricated
Forms	Pellets
Generic	PPA
Processing Method	Water-Heated Mold Injection Molding
RoHS Compliance	RoHS Compliant
Uses	Automotive Applications
	Automotive Electronics
	Automotive Under the Hood
	Connectors
	General Purpose
	Housings
	Industrial Applications
	Industrial Parts
	Machine/Mechanical Parts
	Metal Replacement
	Valves/Valve Parts