- Solvay Specialty Polymers Amodel® AT-6115 HS Polyphthalamide (PPA), 15% Glass Fiber (Dry)
Solvay Specialty Polymers Amodel® AT-6115 HS Polyphthalamide (PPA), 15% Glass Fiber (Dry)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 20% Glass Fiber Reinforced |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Amodel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Amodel® AT-6115 HS Polyphthalamide (PPA), 15% Glass Fiber (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Amodel® AT-6115 HS is a 15% glass-fiber reinforced, toughened grade of polyphthalamide (PPA) resin designed to possess more elongation than other 15% glass-fiber reinforced grades of Amodel resin. This grade was developed for automotive snap-fit electronic connectors. It offers high flow and short molding cycles.Features: Fast Molding Cycle; Good Mold Release; Heat Stabilized; High Elongation; High Flow; Impact Modified; LubricatedUses: Automotive Applications; Automotive Electronics; Automotive Under the Hood; Connectors; General Purpose; Housings; Industrial Applications; Industrial Parts; Machine/Mechanical Parts; Metal Replacement; Valves/Valve PartsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Automotive Specifications ASTM D4000 PPA0123 G15 GB121 KD100 KN042 PN068 YI242; ASTM D6779 PA103G15; DELPHI M-4628 Color: BK324 Black; DELPHI M-4628 Color: NT Natural; FORD WSS-M4D943-A2 Color: BK324 Black; FORD WSS-M4D943-A2 Color: NT Natural; GM GMP.PPA.020 Color: BK-324 Black; GM GMP.PPA.020 Color: NT Natural; GM GMW16363P-PPA-GF15 Color: Black; GM GMW16363P-PPA-GF15 Color: Natural; ISO 1874 PA6T/66-HI, MH, 11-050, GF15Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Filler Content | 15 % | 15 % | Glass Fiber |
| Water Absorption | 0.20 % @Time 86400 sec |
0.20 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm | 0.010 in/in | |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 68.3 MPa @Temperature 100 °C |
9910 psi @Temperature 212 °F |
2; ISO 527-2 |
| 126 MPa @Temperature 23.0 °C |
18300 psi @Temperature 73.4 °F |
2; ISO 527-2 | |
| Tensile Strength | 122 MPa | 17700 psi | ASTM D638 |
| Elongation at Break | 3.4 % | 3.4 % | ASTM D638 |
| 4.1 % @Temperature 23.0 °C |
4.1 % @Temperature 73.4 °F |
ISO 527-2 | |
| 7.7 % @Temperature 100 °C |
7.7 % @Temperature 212 °F |
ISO 527-2 | |
| Tensile Modulus | 5.38 GPa | 780 ksi | ASTM D638 |
| 3.10 GPa @Temperature 100 °C |
450 ksi @Temperature 212 °F |
2; ISO 527-2 | |
| 5.20 GPa @Temperature 23.0 °C |
754 ksi @Temperature 73.4 °F |
2; ISO 527-2 | |
| Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
| 66.9 MPa @Temperature 100 °C |
9700 psi @Temperature 212 °F |
2; ISO 178 | |
| 170 MPa @Temperature 23.0 °C |
24700 psi @Temperature 73.4 °F |
2; ISO 178 | |
| Flexural Modulus | 4.41 GPa | 640 ksi | ASTM D790 |
| 2.34 GPa @Temperature 100 °C |
339 ksi @Temperature 212 °F |
ISO 178 | |
| 4.27 GPa @Temperature 23.0 °C |
619 ksi @Temperature 73.4 °F |
ISO 178 | |
| Compressive Strength | 100 MPa | 14500 psi | ASTM D695 |
| Shear Strength | 56.5 MPa | 8190 psi | ASTM D732 |
| Izod Impact, Notched | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.50 J/cm | 15.9 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | Type 1, Notch A; ISO 180 |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | Type 1; ISO 180 |
| Charpy Impact Unnotched | 7.60 J/cm² | 36.2 ft-lb/in² | Type 1, Edgewise; ISO 179 |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | Type 1, Edgewise; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature 0.000 - 100 °C |
12.2 µin/in-°F @Temperature 32.0 - 212 °F |
2 |
| 30.0 µm/m-°C @Temperature 100 - 200 °C |
16.7 µin/in-°F @Temperature 212 - 392 °F |
2 | |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 0.000 - 100 °C |
50.0 µin/in-°F @Temperature 32.0 - 212 °F |
TMA; ASTM E831 |
| 120 µm/m-°C @Temperature 100 - 200 °C |
66.7 µin/in-°F @Temperature 212 - 392 °F |
TMA; ASTM E831 | |
| Melting Point | 305 °C | 581 °F | ASTM D3418 |
| 305 °C | 581 °F | ISO 11357-3 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 298 °C | 568 °F | HDT B; Unannealed; ISO 75-2/B |
| Deflection Temperature at 1.8 MPa (264 psi) | 251 °C | 484 °F | Unannealed; ISO 75-2/A |
| 260 °C | 500 °F | Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 316 - 324 °C | 601 - 615 °F | |
| Front Barrel Temperature | 327 - 332 °C | 621 - 630 °F | |
| Melt Temperature | 321 - 335 °C | 610 - 635 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 110 °C @Time 14400 sec |
230 °F @Time 4.00 hour |
|
| Moisture Content | <= 0.045 % | <= 0.045 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Heat Stabilizer | |
| Impact Modifier | ||
| Lubricant | ||
| Mold Release | ||
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black; Natural | |
| Form | Pellets | |
| Processing Technique | Water-Heated Mold Injection Molding | |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Network Polymers SAN 300 Natural
- PolyOne Geon™ Vinyl Flexible XV3859 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Polykemi AB POLYfill PPC K5040 E30 Polypropylene Copolymer, Mineral Reinforced, Elastomer Modified
- MMCC Al/Al2O3 Continuous Fiber Aluminum Matrix Composite
- Lucent Polymers PC-1406 Polycarbonate, Extrusion/Blow Molding Grade
- Fainplast Compounds MPH 45/K Medical Flexible PVC, Extrusion
- Ashley Polymers Ashlene® 990L-50G Nylon 610, 50% Glass Reinforced
- Teknor Apex Sarlink® 3480 Thermoplastic Elastomer
Copyright © lookpolymers.com All Rights Reserved