Samsung Cheil Industries Starex® SF-0505H MABS, Unreinforced Scratch Resistant

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Samsung, Cheil Industries
Trade Name Starex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Starex® SF-0505H MABS, Unreinforced Scratch Resistant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0030 - 0.0060 cm/cm
0.0030 - 0.0060 in/in
ASTM D955
Melt Flow 16 g/10 min
16 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115
115
ASTM D785
Tensile Strength at Break 39.2 MPa
5690 psi
ASTM D638
Tensile Strength, Yield 53.9 MPa
7820 psi
ASTM D638
Elongation at Break 11 %
11 %
ASTM D638
Tensile Modulus 2.35 GPa
341 ksi
ASTM D638
Flexural Strength 75.5 MPa
11000 psi
ASTM D790
Flexural Modulus 2.35 GPa
341 ksi
ASTM D790
Izod Impact, Notched 0.981 J/cm

@Thickness 6.35 mm
 1.84 ft-lb/in

@Thickness 0.250 in
 ASTM D256
1.08 J/cm

@Thickness 3.17 mm
 2.02 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 92.0 °C

@Thickness 6.40 mm
 198 °F

@Thickness 0.252 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 84.0 °C

@Thickness 6.40 mm
 183 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 93.0 °C
199 °F
B/50; ISO R306
96.0 °C
205 °F
B/120; ISO R306
Flammability, UL94 HB

@Thickness 1.50 - 3.00 mm
 HB

@Thickness 0.0591 - 0.118 in
Descriptive Properties Value Comments
Pencil Hardness F
500g, JIS K 5401