SABIC Innovative Plastics LNP LUBRICOMP KP003AXZ Acetal Homopolymer

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP KP003AXZ Acetal Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* KP003AXZ is a compound based on Acetal Homopolymer resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant.
Physical Properties Metric English Comments
Density 1.47 g/cc
0.0531 lb/in³
ASTM D792
1.47 g/cc
0.0531 lb/in³
ISO 1183
Moisture Absorption 0.300 %
0.300 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.024 cm/cm

@Time 86400 sec
0.024 in/in

@Time 24.0 hour
ASTM D955
0.024 cm/cm

@Time 86400 sec
0.024 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.025 cm/cm

@Time 86400 sec
0.025 in/in

@Time 24.0 hour
ASTM D955
0.025 cm/cm

@Time 86400 sec
0.025 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 52.0 MPa
7540 psi
ASTM D638
53.0 MPa
7690 psi
ISO 527
Tensile Strength, Yield 53.0 MPa
7690 psi
ASTM D638
53.0 MPa
7690 psi
ISO 527
Elongation at Break 15.1 %
15.1 %
ISO 527
28.8 %
28.8 %
ASTM D638
Elongation at Yield 15 %
15 %
ISO 527
20.9 %
20.9 %
ASTM D638
Tensile Modulus 2.57 GPa
373 ksi
1 mm/min; ISO 527
2.75 GPa
399 ksi
50 mm/min; ASTM D638
Flexural Strength 65.0 MPa
9430 psi
ISO 178
Flexural Modulus 2.75 GPa
399 ksi
ASTM D790
3.00 GPa
435 ksi
ISO 178
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 10.14 J/cm
19.00 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 53.0 kJ/m²
25.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 1.00 J
0.738 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.21
0.21
ASTM D3702 Modified
Coefficient of Friction, Static 0.11
0.11
ASTM D3702 Modified
K (wear) Factor 22.2 x 10-8 mm³/N-M
11.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 95.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
53.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
96.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
53.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 95.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
53.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
96.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
53.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 157 °C
315 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
162 °C

@Thickness 3.20 mm
324 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 88.0 °C
190 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
92.0 °C

@Thickness 3.20 mm
198 °F

@Thickness 0.126 in
unannealed; ASTM D648