- Solvay Specialty Polymers Amodel® AS-4133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry)
Solvay Specialty Polymers Amodel® AS-4133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Amodel® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Amodel® AS-4133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Amodel® AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Testing conducted on samples dry as molded and samples conditioned to 50% relative humidity in accordance with ISO-1110, Accelerated Method. Typical applications include electrical and electronic components especially for automotive systems. Features: Fast Molding Cycle; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; Heat Stabilized; High Heat Resistance; High Strength; Hot Water Moldability; Laser Weldable; Low Moisture Absorption; LubricatedUses: Automotive Applications; Automotive Electronics; Automotive Under the Hood; Cell Phones; Connectors; Electrical/Electronic Applications; General Purpose; Industrial Applications; Industrial Parts; Lawn and Garden Equipment; Machine/Mechanical Parts; Metal Replacement; Thick-walled Parts; Valves/Valve PartsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Additional Properties: Transmittance - ASTM D1003 (1.60 mm): > 20 %; Transmittance - ASTM D1003 (1.60 mm): > 20 %Automotive Specifications ASTM D4000 PA102 G35 Color: BK324 Black; ASTM D4000 PA102 G35 Color: NT Natural; ASTM D4000 PPA0121 G34 GB145 KD170 KN100 PN060 YI285 Color: BK324 Black; ASTM D4000 PPA0121 G34 GB145 KD170 KN100 PN060 YI285 Color: NT Natural; ASTM D6779 PA102G35; BOSCH N28 BN05-OX2 BN0515-GF35-3Anf01AM Color: NT Natural; BOSCH N28 BN05-OX2 BN0515-GF35-3Asw01AM Color: BK324 Black; CHRYSLER MS-DB-478 Type A CPN3598 Color: BK Black; CHRYSLER MS-DB-478 Type A CPN3972 Color: Natural; DELPHI M-2396 Color: BK324 Black; DELPHI M-2396 M2396001 Color: NT Natural; DELPHI M-2396 M2396002 Color: BK-324 Black; DELPHI M-2396 M239600x Color: BU474 Blue; DELPHI M-53291 Color: BU474 Blue; DELPHI M-53293 Color: BK324 Black; DELPHI M-53293 Color: NT Natural; DELPHI M-6081 Color: NT Natural; DELPHI M-6083 Color: BK324 Black; GM GMP.PPA.002 Color: BK324 Black; GM GMP.PPA.002 Color: NT Natural; GM GMW16357P-PPA-GF35 Color: Black; GM GMW16357P-PPA-GF35 Color: Natural; ISO 1874 PA6T/66, MH, 12-120, GF33 Color: BK324 Black; ISO 1874 PA6T/66, MH, 12-120, GF33 Color: NT Natural; TORRINGTON T-456 Color: BK324 Black; TRW S-13972700 Color: BK324 Black; TRW S-13972700 Color: NT Natural; TYCO 100-1392 Color: BK324 Black; TYCO 100-1392 Color: NT Natural; YAZAKI YPES-25-02-306 Color: BK324 Black; YAZAKI YPES-25-02-306 Color: NT NaturalInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Filler Content | 33 % | 33 % | Glass Fiber |
| Water Absorption | 0.29 % @Time 86400 sec |
0.29 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 79.3 MPa @Temperature 175 °C |
11500 psi @Temperature 347 °F |
4; ISO 527-2 |
| 87.6 MPa @Temperature 150 °C |
12700 psi @Temperature 302 °F |
4; ISO 527-2 | |
| 125 MPa @Temperature 100 °C |
18100 psi @Temperature 212 °F |
4; ISO 527-2 | |
| 211 MPa @Temperature 23.0 °C |
30600 psi @Temperature 73.4 °F |
4; ISO 527-2 | |
| Tensile Strength | 200 MPa | 29000 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| 2.6 % @Temperature 23.0 °C |
2.6 % @Temperature 73.4 °F |
ISO 527-2 | |
| 4.3 % @Temperature 100 °C |
4.3 % @Temperature 212 °F |
ISO 527-2 | |
| 6.6 % @Temperature 175 °C |
6.6 % @Temperature 347 °F |
ISO 527-2 | |
| 6.6 % @Temperature 150 °C |
6.6 % @Temperature 302 °F |
ISO 527-2 | |
| Tensile Modulus | 11.7 GPa | 1700 ksi | ASTM D638 |
| 4.83 GPa @Temperature 175 °C |
701 ksi @Temperature 347 °F |
4; ISO 527-2 | |
| 5.31 GPa @Temperature 150 °C |
770 ksi @Temperature 302 °F |
4; ISO 527-2 | |
| 6.83 GPa @Temperature 100 °C |
991 ksi @Temperature 212 °F |
4; ISO 527-2 | |
| 12.6 GPa @Temperature 23.0 °C |
1830 ksi @Temperature 73.4 °F |
4; ISO 527-2 | |
| Flexural Strength | 290 MPa | 42100 psi | ASTM D790 |
| 99.3 MPa @Temperature 175 °C |
14400 psi @Temperature 347 °F |
4; ISO 178 | |
| 111 MPa @Temperature 150 °C |
16100 psi @Temperature 302 °F |
4; ISO 178 | |
| 177 MPa @Temperature 100 °C |
25700 psi @Temperature 212 °F |
4; ISO 178 | |
| 296 MPa @Temperature 23.0 °C |
42900 psi @Temperature 73.4 °F |
4; ISO 178 | |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| 4.21 GPa @Temperature 175 °C |
611 ksi @Temperature 347 °F |
ISO 178 | |
| 4.62 GPa @Temperature 150 °C |
670 ksi @Temperature 302 °F |
ISO 178 | |
| 7.17 GPa @Temperature 100 °C |
1040 ksi @Temperature 212 °F |
ISO 178 | |
| 10.4 GPa @Temperature 23.0 °C |
1510 ksi @Temperature 73.4 °F |
ISO 178 | |
| Compressive Strength | 179 MPa | 26000 psi | ASTM D695 |
| Poissons Ratio | 0.41 | 0.41 | ASTM E132 |
| Shear Strength | 89.6 MPa | 13000 psi | ASTM D732 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.60 J/cm | 18.0 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 9.70 kJ/m² | 4.62 ft-lb/in² | Type 1, Notch A; ISO 180 |
| Izod Impact, Unnotched (ISO) | 59.0 kJ/m² | 28.1 ft-lb/in² | Type 1; ISO 180 |
| Charpy Impact Unnotched | 6.70 J/cm² | 31.9 ft-lb/in² | Type 1, Edgewise; ISO 179 |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | Type 1, Edgewise; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C @Temperature 100 - 200 °C |
8.33 µin/in-°F @Temperature 212 - 392 °F |
2 |
| 20.0 µm/m-°C @Temperature 0.000 - 100 °C |
11.1 µin/in-°F @Temperature 32.0 - 212 °F |
2 | |
| CTE, linear, Transverse to Flow | 76.0 µm/m-°C @Temperature 0.000 - 100 °C |
42.2 µin/in-°F @Temperature 32.0 - 212 °F |
TMA; ASTM E831 |
| 120 µm/m-°C @Temperature 100 - 200 °C |
66.7 µin/in-°F @Temperature 212 - 392 °F |
TMA; ASTM E831 | |
| Melting Point | 327 °C | 621 °F | ISO 11357-3 |
| 327 °C | 621 °F | DSC | |
| Maximum Service Temperature, Air | 210 °C | 410 °F | Continuous Use |
| Deflection Temperature at 0.46 MPa (66 psi) | 320 °C @Thickness 3.20 mm |
608 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 294 °C | 561 °F | Unannealed; ISO 75-2/A |
| 300 °C @Thickness 3.20 mm |
572 °F @Thickness 0.126 in |
Annealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.8 @Frequency 60.0 Hz |
3.8 @Frequency 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 20.0 kV/mm @Thickness 1.60 mm |
508 kV/in @Thickness 0.0630 in |
ASTM D149 |
| Dissipation Factor | 0.0040 @Frequency 60.0 Hz |
0.0040 @Frequency 60.0 Hz |
ASTM D150 |
| 0.012 @Frequency 1.00e+6 Hz |
0.012 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Comparative Tracking Index | 600 V | 600 V | UL 746 |
| High Voltage Arc-Tracking Rate, HVTR | 14.0 mm/min | 0.551 in/min | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 318 - 324 °C | 604 - 615 °F | |
| Front Barrel Temperature | 327 - 332 °C | 621 - 630 °F | |
| Melt Temperature | 329 - 343 °C | 624 - 649 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 120 °C @Time 14400 sec |
248 °F @Time 4.00 hour |
|
| Moisture Content | <= 0.045 % | <= 0.045 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Heat Stabilizer | |
| Lubricant | ||
| Mold Release | ||
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black; Natural | |
| Form | Pellets | |
| Processing Technique | Water-Heated Mold Injection Molding | |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Hyosung Topilene HB242P PP
- Gromax BFG30-FU00B3 Nylon 6 30% Glass Filled (Conditioned)
- Solvay Specialty Polymers Polymist® F5A Polytetrafluoroethylene (PTFE)
- Stratasys® Polyphenylsulfone
- Unifrax Fiberfrax® Durablanket® HP-S Ceramic Fiber Insulator
- Hexcel® HexPly® 954-2A Curing Cyanate Resin, K1100 Fiber
- ELASTO UK Dryflex® 420351S SBS Based Material, 35D Hardness, Natural
- Elgiloy® Co-Cr-Ni Alloy, Wire, 20% Cold Reduction, Heat Treated
- SABIC Innovative Plastics Lexan® 953A PC (Europe-Africa-Middle East)
Copyright © lookpolymers.com All Rights Reserved