Solvay Specialty Polymers Amodel® AFA-6145 V0 Z Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AFA-6145 V0 Z Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel AFA-6145 V0 Z is a 45% glass-fiber reinforced, flame retardant grade of polyphthalamide (PPA) resin specifically formulated for connector applications requiring compatibility with both infrared and vapor phase soldering operations typically used by the electronics industry. Amodel AFA-6145 V0 Z offers high flow and short molding cycles, thereby enhancing molding productivity and lowering costs. - Black: AFA-6145 V0 Z BK 324Injection Notes: Injection Rate: 3 to 4 in/sec Adjust holding pressure to 1/2 injection pressure. Set hold time to maximize part weight. A general purpose screw is recommended, with minimum back pressure.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.80 g/cc
0.0650 lb/in³
ISO 1183/A
Filler Content 45 %
45 %
Glass Fiber Reinforcement
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0040 cm/cm
0.0040 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 193 MPa
28000 psi
ASTM D638
Elongation at Break 1.5 %
1.5 %
ASTM D638
Flexural Strength 276 MPa
40000 psi
ASTM D790
Flexural Modulus 15.5 GPa
2250 ksi
ASTM D790
Izod Impact, Notched 1.10 J/cm
2.06 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Melting Point 310 °C
590 °F
Peak; ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 277 °C
531 °F
Unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 0.794 mm
V-0

@Thickness 0.0313 in
UL 94
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
ASTM D257
Dielectric Constant 4.1

@Frequency 1.00e+6 Hz
4.1

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 23.0 kV/mm

@Thickness 1.59 mm
584 kV/in

@Thickness 0.0626 in
ASTM D149
Dissipation Factor 0.011

@Frequency 1.00e+6 Hz
0.011

@Frequency 1.00e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Rear Barrel Temperature 316 - 324 °C
601 - 615 °F
Front Barrel Temperature 327 - 332 °C
621 - 630 °F
Melt Temperature 321 - 338 °C
610 - 640 °F
Mold Temperature 65.6 - 93.3 °C
150 - 200 °F
Drying Temperature 120 °C
248 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.045 %
0.045 %
Descriptive Properties Value Comments
Additive Flame Retardant
Appearance Black
Automotive Specifications ASTM D6779 PA104G45
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Flame Retardant
Good Chemical Resistance
Good Dimensional Stability
Good Electrical Properties
Good Stiffness
High Flow
High Strength
Hot Water Moldability
Forms Pellets
Generic PPA
Injection Rate Fast
Processing Method Water-Heated Mold Injection Molding
RoHS Compliance RoHS Compliant
Uses Automotive Applications
Automotive Electronics
Automotive Under the Hood
Cell Phones
Connectors
Housings