Radici Heraform® R 350 Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Radici Group Plastics |
| Trade Name | Heraform® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Radici Heraform® R 350 Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Standard grade for injection molding of thick wall parts, stiff-flowing, extrusion grade for tubes and sheet.Information provided by Radici group.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ISO 1183 |
| Water Absorption | 0.65 % | 0.65 % | ISO 62 |
| Melt Flow | 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | ISO 527 |
| Elongation at Break | 32 % | 32 % | ISO 527 |
| Tensile Modulus | 2.60 GPa | 377 ksi | ISO 527 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 |
| Charpy Impact, Notched | 0.850 J/cm² | 4.04 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | ISO 75 |
| Vicat Softening Point | 151 °C @Load 5.10 kg |
304 °F @Load 11.2 lb |
ISO 306 |
| Flammability, UL94 | HB @Thickness 1.00 mm |
HB @Thickness 0.0394 in |
|
| Shrinkage | 2.2 % @Pressure 100 MPa, Temperature 90.0 °C |
2.2 % @Pressure 14500 psi, Temperature 194 °F |
3 mm |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 69 GF 35 FRT 4 Polypropylene Copolymer, 35% Glass Fiber, Halogen Free and Phosphor Free Flame Retardant
- Overview of materials for Phenolic, Novolac, Heat Resistant Grade, Filled
- 3M Dyneon™ CC603 Custom Fluoropolymer Compound (discontinued **)
- Indium Corp. 3592 Wave Solder Flux, No-Residue
- ELASTO UK Dryflex® 662800S SEBS Based Material, Semi-Filled Qualities, 80A Hardness, Black
- CP-Polymer-Technik Wellamid® 6600 MRGV 25/15 HWCP 25% Mineral and 15% Glass Fiber Nylon 66, Heat Stabilized, Dry
- CPC - Vycom POLYCARVE™ Coextruded High Density Sheet (HDPE)
- Dow Saran® 2032
- BASF Ultradur S 4090 G6 30% Glass Filled PBT
Copyright © lookpolymers.com All Rights Reserved