Sax Polymers SAXAMID 236F6Q32 Nylon 6.6, 30% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Glass Reinforced, Impact Grade
Manufacturer Sax Polymers
Trade Name SAXAMID
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Sax Polymers SAXAMID 236F6Q32 Nylon 6.6, 30% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
SAXAMID 236F6Q32 is a impact-modified polyamide 6.6 injection-molding-grade reinforced with 30% glass fibers and very good flow properties. It is suitable for applications requiring toughness in combination with low creep properties.Information provided by SAX Polymers
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ISO 1183
Viscosity Test 150 cm³/g
150 cm³/g
H<sub>2</sub>SO<sub>4</sub>; ISO 307
Mechanical Properties Metric English Comments
Tensile Strength 120 MPa
17400 psi
5 mm/min; ISO 527-1
Elongation at Break 3.5 %
3.5 %
5 mm/min; ISO 527-1
Tensile Modulus 7.20 GPa
1040 ksi
1 mm/min; ISO 527-1
Flexural Strength 183 MPa
26500 psi
2 mm/min; ISO 178
Flexural Modulus 6.20 GPa
899 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 18.0 kJ/m²

@Temperature -30.0 °C
8.57 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
21.0 kJ/m²

@Temperature 23.0 °C
9.99 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Izod Impact, Unnotched (ISO) 90.0 kJ/m²

@Temperature 23.0 °C
42.8 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
95.0 kJ/m²

@Temperature -30.0 °C
45.2 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1U
Charpy Impact Unnotched 8.30 J/cm²

@Temperature 23.0 °C
39.5 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
8.70 J/cm²

@Temperature -30.0 °C
41.4 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 1.60 J/cm²

@Temperature -30.0 °C
7.61 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
2.00 J/cm²

@Temperature 23.0 °C
9.52 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 237 °C
459 °F
80*10*4 s=60mm; ISO 75-1 a
Vicat Softening Point 228 °C
442 °F
B/120; ISO 306
Processing Properties Metric English Comments
Melt Temperature 270 - 300 °C
518 - 572 °F
Mold Temperature 70.0 - 90.0 °C
158 - 194 °F
Drying Temperature 80.0 °C

@Time 7200 - 21600 sec
176 °F

@Time 2.00 - 6.00 hour
Moisture Content <= 0.20 %
<= 0.20 %