Sax Polymers SAXAMID 226F6T3 Nylon 6.6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 226F6T3 Nylon 6.6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 226F6T3 is a general purpose polyamide 6.6 injection-molding-grade reinforced with 30% glass fibers. It shows its high mechanical strength over a long period and is able to perform at higher temperatures in combination with low friction coefficient and very good wear resistance.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 175 MPa | 25400 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 9.50 GPa | 1380 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 280 MPa | 40600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 8.20 GPa | 1190 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 12.0 kJ/m² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 67.0 kJ/m² @Temperature -30.0 °C |
31.9 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 80.0 kJ/m² @Temperature 23.0 °C |
38.1 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 8.30 J/cm² @Temperature 23.0 °C |
39.5 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 250 °C | 482 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPC T16020 Polypropylene Copolymer, Mineral Reinforced
- KKPC Kuhmo HFH 404 Flame Retarded HIPS
- DSM Biomedical BioSpan® S SPU Segmented Polyether Polyurethane (SPU)
- Braskem BF 0323/12 HC LDPE Blown Film Extrusion Polyethylene
- Aptek 2214-A/B Low modulus urethane ESD coating/adhesive
- Austin Novel Materials Texalan® 264D Polyester-based TPU
- Borealis Supercure™ LS4201S Polyethylene Insulation Compound, Crosslinkable
- Solvay RHODASURF® BC-840 Surfactant
- Sumitomo Bakelite North America FM 4005X4649 Fiberglass Reinforced Phenolic Novolac
- Cheng Yu Plastic IPS666N Electric Resisting HIPS
Copyright © lookpolymers.com All Rights Reserved