Sax Polymers SAXAMID 126F3 Nylon 6, 15% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 126F3 Nylon 6, 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 126F3 is a polyamide 6 injection-molding-grade reinforced with 15% glass fibers.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 130 MPa | 18900 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 6.00 GPa | 870 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 212 MPa | 30700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.80 GPa | 696 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 36.0 kJ/m² @Temperature -30.0 °C |
17.1 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 45.0 kJ/m² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 3.80 J/cm² @Temperature -30.0 °C |
18.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 4.50 J/cm² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 213 °C | 415 °F | B/120; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
IEC 60695-11-10 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8531 (834-1) (UF) Synthetic Oil
- NanoAmor 99%, OD/WT/L: 40-70/5-30 nm/0.5-5 um Multi-Walled Carbon Nanotubes
- Radici Radilon® A GV H0 30P Nylon 66-GF30
- SABIC Innovative Plastics Lexan® FXE124R PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP LUBRICOMP DFL22 PC (Asia Pacific)
- Kuraray HYBRAR® F1 Foam Compound
- Teknor Apex Sinvicomp SRF 3704 Polyvinyl Chloride, Rigid
- ChevronTexaco Elite-Cut® AD Metal Working Fluid
Copyright © lookpolymers.com All Rights Reserved