- Sax Polymers SAXALEN PPH303G20 Polypropylene Homopolymer, 20% Glass Filled
Sax Polymers SAXALEN PPH303G20 Polypropylene Homopolymer, 20% Glass Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | Sax Polymers |
| Trade Name | SAXALEN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXALEN PPH303G20 Polypropylene Homopolymer, 20% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXALEN PPH303G20 is a 20% glass filled Polypropylene - Homopolymer injection molding grade with good stiffness.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | |
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 230 °C |
11 g/10 min @Load 4.76 lb, Temperature 446 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 59.0 MPa | 8560 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 4.40 GPa | 638 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 97.0 MPa | 14100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.90 GPa | 566 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 34.0 kJ/m² @Temperature 23.0 °C |
16.2 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 3.30 J/cm² @Temperature -30.0 °C |
15.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 4.20 J/cm² @Temperature 23.0 °C |
20.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 136 °C | 277 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 130 °C | 266 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 250 °C | 428 - 482 °F | |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F |
Users viewing this material also viewed the following:
- Flint Hills P4G4Z-011 Homopolymer Polypropylene
- Garlock 9122 Nitrile Sheet Rubber Gasketing
- Spartech Polycast SAR (Super Abrasion Resistant) Cell Cast Acrylic
- Zotefoams Evazote® EV50 Ethylene Vinyl Acetate Copolymer Foam
- Eastman Tenite 360E2R30016 Cellulose Acetate Propionate, Natural, Trsp
- Covestro Bayblend® ET3032 FR Rubber Modified PC Blend, 10% Mineral Filled
- ChevronTexaco TEGRA® ISO 68 Synthetic Compressor Oil
- Aptek DI-STRATE 95211 Microwave/RF Foam Substrate
- Mueller Ecostream™ C36500 Uninhibited Leaded Muntz Metal
Copyright © lookpolymers.com All Rights Reserved