Cadi 10 MOLD-MOR™

Category Metal , Nonferrous Metal , Copper Alloy
Manufacturer Cadi Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Cadi 10 MOLD-MOR™.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A Copper Nickel Silicon Chromium Alloy with high thermal conductivity and moderate hardness.Information provided by Cadi Company.
Physical Properties Metric English Comments
Density 8.80 g/cc
0.318 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell B 95
95
Tensile Strength at Break >= 607 MPa

@Thickness >=50.8 mm
 >= 88000 psi

@Thickness >=2.00 in
>= 621 MPa

@Thickness 25.4 - 50.8 mm
 >= 90000 psi

@Thickness 1.00 - 2.00 in
>= 648 MPa

@Thickness <=25.4 mm
 >= 94000 psi

@Thickness <=1.00 in
Tensile Strength, Yield >= 607 MPa

@Strain 0.500 %,
Thickness >=50.8 mm
 >= 88000 psi

@Strain 0.500 %,
Thickness >=2.00 in
>= 621 MPa

@Strain 0.500 %,
Thickness 25.4 - 50.8 mm
 >= 90000 psi

@Strain 0.500 %,
Thickness 1.00 - 2.00 in
>= 648 MPa

@Strain 0.500 %,
Thickness <=25.4 mm
 >= 94000 psi

@Strain 0.500 %,
Thickness <=1.00 in
Modulus of Elasticity 131 GPa
19000 ksi
Thermal Properties Metric English Comments
Thermal Conductivity 225 W/m-K
1560 BTU-in/hr-ft²-°F
Melting Point 1068 °C
1955 °F
Liquidus 1068 °C
1955 °F
Component Elements Properties Metric English Comments
Chromium, Cr 0.50 %
0.50 %
Copper, Cu 96.5 %
96.5 %
Nickel, Ni 2.4 %
2.4 %
Silicon, Si 0.60 %
0.60 %
Electrical Properties Metric English Comments
Electrical Resistivity <= 0.00000383 ohm-cm
<= 0.00000383 ohm-cm
Calculated from Min 45 %IACS, up to 3" diameter/any thickness
Processing Properties Metric English Comments
Processing Temperature 649 °C
1200 °F
Brazing, <15 minutes
Descriptive Properties Value Comments
RMWA Class 3
Users viewing this material also viewed the following: