- Sax Polymers SAXALEN PPC343G20 Polypropylene Copolymer, 20% Glass Filled
Sax Polymers SAXALEN PPC343G20 Polypropylene Copolymer, 20% Glass Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | Sax Polymers |
| Trade Name | SAXALEN |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXALEN PPC343G20 Polypropylene Copolymer, 20% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXALEN PPC343G20 is a 20% glass filled Polypropylene - Copolymer intended for injection molding.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C |
20 g/10 min @Load 4.76 lb, Temperature 446 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 47.0 MPa | 6820 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 3.90 GPa | 566 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 76.0 MPa | 11000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.20 GPa | 464 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 11.0 kJ/m² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 32.0 kJ/m² @Temperature -30.0 °C |
15.2 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 34.0 kJ/m² @Temperature 23.0 °C |
16.2 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 117 °C | 243 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 103 °C | 217 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 250 °C | 428 - 482 °F | |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F |
Users viewing this material also viewed the following:
- PPT BP125 NiZn Ferrite Powder
- PolyOne Nymax™ GF 1800 35 HS Natural Polyamide 612 (Nylon 612)
- Lehmann & Voss LUVOCOM® 20-7913 Polyphthalamide, with carbon fiber
- Teknor Apex Flexalloy® 9300-80 Polyvinyl Chloride Elastomer
- Wanhua Chemical Wanthane® WHT-A885 Aliphatic TPU
- EMS-Griltech Griltex® D 1365E Copolyester Hotmelt Adhesive (Technical Applications)
- EMS-Griltech Griltex® D 1533E Copolyester Hotmelt Adhesive (Technical Applications)
- CP-Polymer-Technik Wellamid® 6000 MX 400 CP Combination Nylon 6, Heat Stabilized, Dry
- 3M Scotch-Weld™ MG77 AC Medical Grade Instant Adhesive Primer
- Momentive Performance Materials Addisil™ 2040 E Industrial Extrusion Heat Cured Rubber
Copyright © lookpolymers.com All Rights Reserved