MarkeTech H-4 Honeycomb Ceramic
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | MarkeTech |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | MarkeTech H-4 Honeycomb Ceramic.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
MarkeTech International special honeycomb ceramics have a uniform lattice structure, low expansion coefficient, good thermal shock resistance, higher specific surface area, low-pressure drop, and low density. They are available in cordierite or mullite ceramic. Cordierite honeycomb ceramics are mainly used as catalyst support for the automobile and for purification waste gas of industrial organic processing, and as filters in melting metal.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.450 g/cc | 0.0163 lb/in³ | |
| Water Absorption | 25 - 30 % | 25 - 30 % | |
| Porosity | 45 - 50 % | 45 - 50 % | |
| Specific Surface Area | 5.0 - 10 m²/g | 5.0 - 10 m²/g |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Compressive Strength | >= 4.00 MPa | >= 580 psi | Perpendicular to holes |
| >= 12.0 MPa | >= 1740 psi | Parallel to holes |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 1.50 - 1.80 µm/m-°C | 0.833 - 1.00 µin/in-°F | |
| Melting Point | 1360 °C | 2480 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Hole Density | 400/inch | |
| Wall Thickness | 0.25 mm |
Users viewing this material also viewed the following:
- PTS Tristar® PC-10R-CL(15) 15 MFI Clear Polycarbonate with Release
- Materion Beryllium Copper Alloy 25 Strip; A -Planished (TB00) Temper (UNS C17200)
- Saint-Gobain Chemfab® 1580 PTFE Coated Fiberglass Conveyor Belting
- Teknor Apex Sinpolene MBW0141 Linear Low Density Polyethylene
- A. Schulman ComAlloy® 510-3010 10% Glass Fiber Reinforced Polycarbonate
- A. Schulman COMTUF® 464 Glass Reinforced Impact Modified PBT Alloy
- Tra-Con Tra-Bond 546S05 Dual-Cure Acrylate
- Covestro Desmopan® 150 Thermoplastic Polyurethane
- Diamond Polymers NPP25-0802 30G Chemically Couple Glass Filled Copolymer Polypropylene
- Overview of materials for High Density Polyethylene (HDPE), Rotational Molding Grade
Copyright © lookpolymers.com All Rights Reserved