ExxonMobil Metallyte™ 18MM483 OPP Film

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer	Exxon Chemical
Trade Name	Metallyte™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Metallyte™ 18MM483 OPP Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: A biaxially oriented polypropylene film, metalized on one side with a broad seal range surface on the other side. This film is designed for high barrier performance packaging applications. Designed to be used in single web on HFFS or laminated to other substrates on all types of packaging machines.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Excellent adhesion of aluminum to filmExcellent oxygen barrierExcellent moisture barrierExcellent light barrierVery good hot tackVery broad seal rangeHigh yieldBrilliant metal appearanceFeatures: Flavor & Aroma BarrierGas BarrierIn Lamination Lap SealableLight BarrierMoisture BarrierOxygen BarrierApplications: Biscuits/Cookie/CrackersConfectionery, Chocolate Confectionery, Gum Confectionery, Sugar Crisps and SnacksDry Foods and Beverage PowdersFrozen FoodPet Food Uses: HFFS Flexible PackagingPre-made Bags – Flexible Packaging VFFS Flexible Packaging Processing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Solvent Flexographic Printing and Surface Print UnsupportedInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Water Vapor Transmission	0.101 g/m²/day @Temperature 23.0 °C	0.00650 g/100 in²/day @Temperature 73.4 °F	85% RH; ExxonMobil Method
	0.101 g/m²/day @Temperature 25.0 °C	0.00650 g/100 in²/day @Temperature 77.0 °F	75% RH; ExxonMobil Method
	0.202 g/m²/day @Temperature 38.0 °C	0.0130 g/100 in²/day @Temperature 100 °F	90% RH; ExxonMobil Method
Oxygen Transmission Rate	26.1 cc/m²/day @Temperature 23.0 °C	1.68 cc/100 in²/day @Temperature 73.4 °F	Wet, 75% RH; ExxonMobil Method
	26.4 cc/m²/day @Temperature 23.0 °C	1.70 cc/100 in²/day @Temperature 73.4 °F	0% RH; ExxonMobil Method
Thickness	18.0 microns	0.710 mil	ExxonMobil Method
Coating Weight	16.2 g/m²	10.1 lb/ream	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	160 %	160 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD	55 %	55 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity	2.00 GPa	290 ksi	MD; ExxonMobil Method
	3.70 GPa	537 ksi	TD; ExxonMobil Method
Seal Strength	460 g/25 mm @Pressure 0.276 MPa, Temperature 140 °C	460 g/in @Pressure 40.0 psi, Temperature 284 °F	Otto Brugger, 0.2 sec; ExxonMobil Method
Film Tensile Strength at Break, MD	140 MPa	20300 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD	260 MPa	37700 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method

Thermal Properties	Metric	English	Comments
Shrinkage, MD	4.0 % @Temperature 135 °C, Time 432 sec	4.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method
Shrinkage, TD	4.0 % @Temperature 135 °C, Time 432 sec	4.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method

Optical Properties	Metric	English	Comments
Optical Density	2.5	2.5	ExxonMobil Method

Descriptive Properties	Value	Comments
Heat Seal Range	99°F	36.3 psi, 0.2 sec
Yield	43000 in²/lb