Samyang Tripet® 2500G30 Polyethylene Terephthalate, 30% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced |
| Manufacturer | Samyang |
| Trade Name | Tripet® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Tripet® 2500G30 Polyethylene Terephthalate, 30% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TRIPET® has excellent heat resistance, good surface, chemical resistance and high electrical performance.Applications:Coil BobbinConnectorMotor HousingLamp HousingRelay BaseIron bodyAll information provided by Samyang
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Thickness 3.00 mm |
0.0020 - 0.0040 in/in @Thickness 0.118 in |
ASTM D955 |
| Melt Flow | 65 g/10 min @Load 5.00 kg, Temperature 265 °C |
65 g/10 min @Load 11.0 lb, Temperature 509 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 162 MPa | 23500 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Yield Strength | 230 MPa | 33400 psi | ASTM D790 |
| Flexural Modulus | 8.83 GPa | 1280 ksi | ASTM D790 |
| Izod Impact, Unnotched | 0.883 J/cm @Thickness 3.17 mm |
1.65 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM D696 |
| Melting Point | 255 °C | 491 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | ASTM D149 |
| Dissipation Factor | 0.013 @Frequency 1.00e+6 Hz |
0.013 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 125 sec | 125 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Chevron Phillips 5758 LDPE High Clarity, High Impact Film Resin (discontinued **)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Cumar W 2 1/2 Plasticizer
- Karina 18/482-FC-LMP (SDB) Gray Color Concentrate for PVC
- Techmer ES HiFill® PA4/6 GF5 IM HS BK 5% Glass Filled
- SMAC SMACMOUNT® 2112S Damping Material
- Teknor Apex Telcar® TL-1522B Thermoplastic Elastomer
- Trelleborg Emerson & Cuming Stycast® 2741LV/15LV Two-Component Easy Mix Ratio Encapsulant
- Entec Hyrene® PSCRY 1.5 General Purpose Polystyrene
- BASF Neopor® 2400 Expandable Polystyrene
- Austin Novel Materials Texalan® 685A Polyester and Polyether based TPU
Copyright © lookpolymers.com All Rights Reserved