SABIC Innovative Plastics LNP THERMOCOMP DC006 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DC006 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* DC006 is a compound based on Polycarbonate resin containing Carbon Fiber.This product is also known as Thermocomp* DC-1006.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.120 % | 0.120 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00090 cm/cm | 0.00090 in/in | SABIC Method |
| 0.0010 - 0.0020 cm/cm @Time 86400 sec |
0.0010 - 0.0020 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0033 cm/cm | 0.0033 in/in | SABIC Method |
| 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 141 MPa | 20500 psi | Type I, 5 mm/min; ASTM D638 |
| 141 MPa | 20500 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 141 MPa | 20500 psi | Type I, 5 mm/min; ASTM D638 |
| 141 MPa | 20500 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| 1.9 % | 1.9 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.8 % | 1.8 % | 5 mm/min; ISO 527 |
| 1.9 % | 1.9 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 15.78 GPa | 2289 ksi | 1 mm/min; ISO 527 |
| 15.87 GPa | 2302 ksi | 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 192 MPa | 27800 psi | 2 mm/min; ISO 178 |
| 195 MPa | 28300 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 14.3 GPa | 2070 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.87 J/cm | 11.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 44.0 kJ/m² | 20.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J | 8.85 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 44.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
24.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 11.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
6.11 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 20.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 148 °C | 298 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 147 °C @Thickness 3.20 mm |
297 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- RheTech Products HP531-680UV 22% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, Medium Scratch Resistant, BJAA Light Parchment
- Nanocyl NANOCYL™ NC1000 Single-Wall Isolated and Bundled Carbon Nanotubes - Research grade
- DuPont Performance Polymers Zytel® HTN 54G35HSLR NC010 Polyphthalamide (PPA) (Unverified Data**)
- DSM Arnitel® EB500 Polyether Ester Elastomer (European and Asian Grade) (discontinued **)
- Lord Adhesives 7542D Two-Component Urethane Adhesive
- Micropol Microlin LL17 Linear Polyethylene Rotational Molding Powder
- Momentive Performance Materials RTV11 White General Purpose Potting/Encapsulating Compound
- DSM Novamid® 2430A-1 PA666
- Braskem LL 218/21 LLDPE Blown Film Extrusion Polyethylene
- 3M Dyneon™ J14 PTFE Micropowder
Copyright © lookpolymers.com All Rights Reserved