Toyobo PELPRENE™ S2001 Polyester TPE
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Toyobo |
| Trade Name | Pelprene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo PELPRENE™ S2001 Polyester TPE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Polyester TPEInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.38 % | 0.38 % | 23°C, 65% RH |
| Linear Mold Shrinkage | 0.013 cm/cm @Thickness 2.00 mm |
0.013 in/in @Thickness 0.0787 in |
|
| Melt Index of Compound | 16 g/10 min @Temperature 230 °C |
16 g/10 min @Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 97 | 97 | JIS K6301 |
| Hardness, Shore D | 55 | 55 | ASTM D2240 |
| Tensile Strength at Break | 36.0 MPa | 5220 psi | ASTM D638 |
| Elongation at Break | 610 % | 610 % | ASTM D638 |
| 50% Modulus | 0.0167 GPa | 2.42 ksi | ASTM D638 |
| Flexural Modulus | 0.186 GPa | 27.0 ksi | ASTM D790 |
| Compressive Modulus | 0.0163 GPa | 2.36 ksi | 0.1; ASTM D695 |
| Resilience | 60 | 60 | JIS K6301 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tear Strength | 155 kN/m | 884 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 12 | 12 | ASTM D1044 |
| Compression Set | 61 % | 61 % | JIS K6301 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 140 µm/m-°C @Temperature 20.0 °C |
77.8 µin/in-°F @Temperature 68.0 °F |
TMA |
| Melting Point | 206 °C | 403 °F | By DSC |
| Maximum Service Temperature, Air | 107 °C | 225 °F | Heat deflection temperature, load unknown; ASTM D648 |
| Vicat Softening Point | 185 °C | 365 °F | ASTM D1525 |
| Brittleness Temperature | <= -65.0 °C | <= -85.0 °F | JIS K6301 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | JIS K2111 |
Users viewing this material also viewed the following:
- Ineos G60-25-144 HDPE
- Techmer ES Luriblend® PA6/6 GF40 ML2 HS 40% Glass Filled
- DuPont Conpol™ 20B Ethylene-Methacrylic Acid Additive Resin
- Chevron Phillips MarFlex® 7109 LLDPE Blown Film Resin
- DuPont Performance Polymers Zytel® 151 NC010 Nylon 612 (Unverified Data**)
- Arlon HSLW401R##-P0 0.040" (1.02 mm) Self-Fusing Silicone Tape (Triangular, Unsupported)
- ATI Allegheny Ludlum 310Si Austenitic Stainless Steel
Copyright © lookpolymers.com All Rights Reserved