Samyang Triloy® 210NHF Polymer Alloy, Flame Retardancy (Non-Halogen)
| Category | Polymer , Thermoplastic |
| Manufacturer | Samyang |
| Trade Name | Triloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Triloy® 210NHF Polymer Alloy, Flame Retardancy (Non-Halogen).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent impact, formability and weather resistance.210NHF is a flame retardant (non-halogen) grade.Applications: LCD TV Rear Cover (high flow)Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 260 °C |
20 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength | 61.8 MPa | 8960 psi | ASTM D638 |
| Elongation at Break | 90 % | 90 % | ASTM D638 |
| Flexural Yield Strength | 83.4 MPa | 12100 psi | ASTM D790 |
| Flexural Modulus | 2.26 GPa | 327 ksi | ASTM D790 |
| Izod Impact, Notched | 5.39 J/cm @Thickness 3.17 mm |
10.1 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 83.0 µm/m-°C | 46.1 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| 5VB @Thickness 2.50 mm |
5VB @Thickness 0.0984 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 9.00e+16 ohm-cm | 9.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 | 3.0 | ASTM D150 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149 |
| Dissipation Factor | 0.0090 | 0.0090 | ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Overview of materials for Polytetrafluoroethylene (PTFE), Mica Filled
- SABIC Innovative Plastics Ultem 1010A PEI (Europe-Africa-Middle East)
- Silberline SilBerCote® 3500-20Y
- Zircar Ceramics ASBF-1 Alumina-Silica Bulk Fiber
- E-Polymers TEKAMID® TB110M40 , 40% Mineral Filled PA6, DAM
- DuPont Performance Polymers Zytel® 103FHSA NC010 Nylon 66 (Unverified Data**)
- ExxonMobil Santoprene® 241-64 Thermoplastic Elastomer
- Parker Chomerics CHO-BOND 1073, Part A Silicone Resin Mixture
- A. Schulman POLYBATCH™ Hot Pink 50377 Concentrate Based In Polyethylene
- Resinlab® EP1026 Clear Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved