A. Schulman ComAlloy Voloy® 612 Nylon 6, Glass Fiber/Bead Reinforced, Flame Retardant, UL
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Voloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Voloy® 612 Nylon 6, Glass Fiber/Bead Reinforced, Flame Retardant, UL.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.30% Glass Fiber/Bead Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 94.0 MPa | 13600 psi | ASTM D638 |
| Elongation at Break | 3.4 % | 3.4 % | ASTM D638 |
| Flexural Strength | 144 MPa | 20900 psi | ASTM D790 |
| Flexural Modulus | 7.40 GPa | 1070 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.46 J/cm | 4.61 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 205 - 225 °C | 401 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 192 °C | 378 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 260 - 271 °C | 500 - 520 °F |
Users viewing this material also viewed the following:
- Quadrant EPP Semitron® ESd 410C PEI, static dissipative, extruded (ISO Data)
- A. Schulman POLYBLAK™ 3123 Premium Black Color Concentrate, 50% Carbon Black Based In LDPE
- A. Schulman POLYBATCH™ White LL8425 MG Concentrate Based In LLDPE
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR Iceberg Clay Filler
- ChevronTexaco ISO 220 Marine Oil E
- Addiplast Addilene H 211 V20 Polypropylene Homopolymer
- BASF Ultramid® 8262G HS BK-102 7/13% Glass/Mineral Filled PA6 (Dry)
- 3M 4F79 Fire Retardant Polyethylene Carpet Protective Tape
- BASF Ultramid® 1603-2 NF2004 43% Glass Filled PA66 (Dry)
Copyright © lookpolymers.com All Rights Reserved