Samyang TribitÂ® 1510 PBT, Middle Viscosity

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Unreinforced, Molded
Manufacturer	Samyang
Trade Name	Tribit®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Samyang TribitÂ® 1510 PBT, Middle Viscosity.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Crystallization is fast, formability is excellent and thermal resistance, chemical resistance, electrical properties and abrasion resistance are excellent.1510 is a middle viscosity grade.Information provided by Samyang.

Physical Properties	Metric	English	Comments
Specific Gravity	1.30 g/cc	1.30 g/cc	ASTM D792
Water Absorption	0.10 %	0.10 %	ASTM D570
Linear Mold Shrinkage	0.014 - 0.023 cm/cm	0.014 - 0.023 in/in	ASTM D955
Melt Flow	35 g/10 min @Load 2.16 kg, Temperature 235 Â°C	35 g/10 min @Load 4.76 lb, Temperature 455 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	118	118	ASTM D785
Tensile Strength	53.9 MPa	7820 psi	ASTM D638
Elongation at Break	120 %	120 %	ASTM D638
Flexural Yield Strength	73.5 MPa	10700 psi	ASTM D790
Flexural Modulus	1.96 GPa	284 ksi	ASTM D790
Izod Impact, Notched	0.294 J/cm @Thickness 3.17 mm	0.551 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear	90.0 Âµm/m-Â°C	50.0 Âµin/in-Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	155 Â°C	311 Â°F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	60.0 Â°C	140 Â°F	ASTM D648
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+16 ohm-cm	1.00e+16 ohm-cm	ASTM D257
Dielectric Constant	3.2	3.2	ASTM D150
Dielectric Strength	17.0 kV/mm	432 kV/in	ASTM D149
Dissipation Factor	0.020	0.020	ASTM D150
Arc Resistance	180 sec	180 sec	ASTM D495