- LyondellBasell Microthene® MP574189 Linear Low Density Polyethylene, Injection Molding Grade
LyondellBasell Microthene® MP574189 Linear Low Density Polyethylene, Injection Molding Grade
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded |
| Manufacturer | LyondellBasell (former Equistar) |
| Trade Name | Microthene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LyondellBasell Microthene® MP574189 Linear Low Density Polyethylene, Injection Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ApplicationsMicrothene MP574189 exhibits excellent flow and impact with good stiffness. Typical applications include lids, closures, containers, housewares and medical items. MP574189 is 16 mesh powder and is also available in pellet form Petrothene GA574189.Regulatory StatusMP574189 meets the requirements of the Food and Drug Administration regulation, 21 CFR 177.1520.Processing TechniquesSpecific recommendations for processing MP574189 can only be made when the processing conditions, equipment and end use are known.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | ASTM D1505 |
| Melt Flow | 50 g/10 min | 50 g/10 min | ASTM D1238 |
| Spiral Flow | 45.5 cm | 17.9 in | Equistar |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 60 | 60 | ASTM D2240 |
| Tensile Strength at Break | 8.96 MPa | 1300 psi | 20 in/min; ASTM D638 |
| Tensile Strength, Yield | 15.2 MPa | 2200 psi | 20 in/min; ASTM D638 |
| Elongation at Yield | 11 % | 11 % | 20 in/min; ASTM D638 |
| 1% Secant Modulus | 483 MPa | 70000 psi | 0.5 in/min; ASTM D790 |
| 2% Secant Modulus | 0.421 GPa | 61.0 ksi | 0.5 in/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 47.2 °C | 117 °F | ASTM D648 |
| Vicat Softening Point | 84.4 °C | 184 °F | ASTM D1525 |
| Brittleness Temperature | -72.2 °C | -98.0 °F | ASTM D746 |
| Compliance Properties | Metric | English | Comments |
|---|---|---|---|
| FDA | Yes | Yes |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 177 °C | 350 °F | |
| Middle Barrel Temperature | 191 °C | 375 °F | |
| Front Barrel Temperature | 204 °C | 400 °F | |
| Nozzle Temperature | 204 °C | 400 °F |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE D 4112 BLK
- SABIC Innovative Plastics Lexan® HP4R PC
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 45 PHR Iceberg Clay Filler
- Sylvin Technologies 9940-85 Natural PVC Molding Compound
- SGL Carbon Group PANOX® FB M400 EEA Oxidized Textile Fiber, Milled Fiber, For carbon/carbon and spinning
- Sichuan Deyang Haton® hGR20 Polyphenylene Sulfide, Glass Fiber Reinforced
- Silberline Extra Fine "O" Standard Series
- SABIC Innovative Plastics LNP THERMOCOMP RF0069S PA 66
- Eagle Brass 511 Phosphor Bronzes 4%, Extra Spring
- Daikin NEOFLON NP-21 FEP Pellets
Copyright © lookpolymers.com All Rights Reserved