- Lanxess Pocan® DP CF 2200 000000 PBT+PC
Lanxess Pocan® DP CF 2200 000000 PBT+PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® DP CF 2200 000000 PBT+PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT+PC, non-reinforced, injection molding, flame retardant, impact modified, low tendency to warp
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO 294-4, 2577 |
| Melt Flow | 21 g/10 min @Load 5.00 kg, Temperature 260 °C |
21 g/10 min @Load 11.0 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | ISO 527-1/-2 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ISO 527-1/-2 |
| Elongation at Break | 17 % | 17 % | Nominal; ISO 527-1/-2 |
| Elongation at Yield | 2.8 % | 2.8 % | ISO 527-1/-2 |
| Tensile Modulus | 2.60 GPa | 377 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 61.0 °C | 142 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.3 @Frequency 100 Hz |
3.3 @Frequency 100 Hz |
IEC 60250 | |
| Dissipation Factor | 0.014 @Frequency 1.00e+6 Hz |
0.014 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.025 @Frequency 100 Hz |
0.025 @Frequency 100 Hz |
IEC 60250 | |
| Comparative Tracking Index | 300 V | 300 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shortname | ISO 7792-1-PBT+PC,GFHLMPR,09-020; ISO1043-(PBT+PC) FR(17) | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- Westlake EMAC® SP2405 20% Ethylene-Methyl Acrylate Copolymer (discontinued **)
- Lehmann & Voss LUVOCOM® 1105/GR/15/TF/15-2 PEEK, with PTFE, lubricant modified
- SABIC Innovative Plastics LNP STAT-KON DFD03 PC
- Vyncolit TX10916 Graphite Filled Novolac Phenolic
- Braskem TX7012 LDPE Blown Film Extrusion Polyethylene
- Alliance C-7 Strontium Ferrite Ceramic Magnetic Material
- ExxonMobil Escorene® HD-7835 MMW-HDPE Blown Film Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved