Eurostar Starpylen HU 70E3 HDPE, Injection Molding
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starpylen |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starpylen HU 70E3 HDPE, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starpylen HU 70E3 is a High Density Polypropylene Injection Molding Resin (also known as HU70E3)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.91 g/cc | 0.0690 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 18.0 MPa | 2610 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 25 % | 25 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 0.450 GPa | 65.3 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 33.0 MPa | 4790 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 0.300 GPa | 43.5 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 195 - 205 °C | 383 - 401 °F | |
| Zone 2 | 215 - 225 °C | 419 - 437 °F | |
| Zone 3 | 225 - 250 °C | 437 - 482 °F | |
| Melt Temperature | 225 - 250 °C | 437 - 482 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
| Drying Temperature | 70.0 °C @Time 10800 sec |
158 °F @Time 3.00 hour |
Users viewing this material also viewed the following:
- Parker Chomerics C-Wings Heat Spreaders
- LG Chemical LUMID SG2460B PA66+GF46%, General purpose, Good Surface
- SABIC Innovative Plastics LNP THERMOCOMP DX06313I PC (Asia Pacific)
- A. Schulman SCHULADUR® B GF15 15% Glass Fiber Reinforced PET
- Eastman Aqua PJ003 PET
- ExxonMobil LLDPE LL 6301XR Molding Linear Low Density Polyethylene Resin (European Grade)
- AK Steel ZINCGRIP® Hot Dip Galvanized Carbon Steel, High Strength Low Alloy Steel (HSLA), 055XLK
- Borealis HD214CF Polypropylene Homopolymer
- Buckeye Polymers BP RPP 1010 T Polypropylene, 10% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved