- Acrylonitrile Butadiene Styrene (ABS), Molded
- Samsung Cheil Industries Starex® SD-0170 F ABS, Unreinforced
Samsung Cheil Industries Starex® SD-0170 F ABS, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SD-0170 F ABS, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Melt Flow | 1.7 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.7 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength at Break | 25.5 MPa | 3700 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 31.4 MPa | 4550 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 22 % | 22 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 1.57 GPa | 228 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 49.0 MPa | 7110 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.57 GPa | 228 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 3.73 J/cm @Thickness 6.35 mm |
6.98 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 4.31 J/cm @Thickness 3.17 mm |
8.08 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C @Thickness 6.40 mm |
199 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C @Thickness 6.40 mm |
178 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 92.0 °C | 198 °F | B/50; ISO R306 |
| 96.0 °C | 205 °F | B/120; ISO R306 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® ML7678 PC
- SABIC Innovative Plastics Lexan® FR60 Polycarbonate Film, Flame Retardant
- Michelman® Hydrosize® U6-01 Polyurethane solution
- Styrolution PS 158K GPPS
- Hexcel® HexForce™ 352 Aramid Fabric
- Eastman Tenite 360E461312 Propionate Clear, Trsp
- Aclo Accutech Polypropylene Copolymer CP0437C30L1 Calcium Reinforced
- 3M 4492B Double Coated Polyethylene Foam Tape
- Azoty Tarnow™ Tarnamid® T-27 CF10 Polyamide 6 10% Carbon Fiber - Antistatic and Electroconductive
- M Cubed Technologies ASC-301 Aluminum alloy-30% SiC Metal Matrix Composite
Copyright © lookpolymers.com All Rights Reserved