Lotte Chemical Titan TITANLENE® LDF200GG Low density polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Extrusion Grade |
| Manufacturer | Lotte Chemical Titan Holding Sdn. Bhd. (Former Titan Chemicals) |
| Trade Name | TITANLENE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lotte Chemical Titan TITANLENE® LDF200GG Low density polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LDF200GG is a low density polyethylene resin for film extrusion. LDF200GG has medium slip and anti-block additives. LDF200GG meets the U.S. Food and Drug Administration (FDA) criteria for food contact use as specified in 21 CFR 177.1520 (c) 2.1 & (c) 2.2.Applications: Produce bags T-shirt carrier bags Display packaging Light duty shrink filmAdditives: Medium slip AntiblockAdvantages: Good optical Good mechanical propertiesInformation provided by Titan Chemicals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Base Resin Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Thickness | 30.0 microns | 1.18 mil | extruded at 2.5:1 BUR |
| Base Resin Melt Index | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 310 % | 310 % | ASTM D882 |
| Film Elongation at Break, TD | 580 % | 580 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 6.00 g/micron | 152 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 4.00 g/micron | 102 g/mil | ASTM D1922 |
| Dart Drop | 2.00 g/micron | 50.8 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 26.5 MPa | 3840 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 21.6 MPa | 3130 psi | ASTM D882 |
| 1% Secant Modulus, MD | 205.94 MPa | 29869 psi | ASTM D882 |
| 1% Secant Modulus, TD | 225.56 MPa | 32714 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 95.0 °C | 203 °F | resin; ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 160 - 180 °C | 320 - 356 °F | |
| Blow-up Ratio (BUR) | 2.5 | 2.5 |
Users viewing this material also viewed the following:
- MV Labs MO1040 (NH4)2MoS4 Ammonium tetrathiomolybdate
- Polykemi AB POLYelast TPE ZC100 D40 Thermoplastic Elastomer
- Pacific Sintered Materials FN-255-S(HT) Nickel Steel Powdered Metal
- SABIC Innovative Plastics Cycoloy® CX1440 PC+ABS
- SABIC Innovative Plastics Lexan® HPH4504 PPC
- Lubrizol Advanced Materials Pearlthane® 12C75 Thermoplastic Polyurethane Elastomer
- STAR Thermoplastic Alloys & Rubbers StarTUFF TF 65-HR-1 TPE
- Borealis RF926MO Polypropylene, Transparent Random Copolymer
- A. Schulman POLYBATCH™ XAMF-500-T Process Aid Concentrate, Concentrate Based In LLDPE
- PolyOne Lubri-Tech™ AT-10GF-10KV/000 Acetal-Copolymer, Glass Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved