Samsung Cheil Industries StarexÂ® LX-0989EXS ABS, Unreinforced Metallic-Look

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer	Samsung, Cheil Industries
Trade Name	Starex®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Samsung Cheil Industries StarexÂ® LX-0989EXS ABS, Unreinforced Metallic-Look.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries.

Physical Properties	Metric	English	Comments
Specific Gravity	1.09 g/cc	1.09 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0070 - 0.0080 cm/cm @Thickness 3.20 mm	0.0070 - 0.0080 in/in @Thickness 0.126 in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0065 cm/cm @Thickness 3.20 mm	0.0065 in/in @Thickness 0.126 in	ASTM D955
Melt Flow	10 g/10 min @Load 10.0 kg, Temperature 220 Â°C	10 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	110	110	ASTM D785
Tensile Strength at Break	36.3 MPa	5260 psi	5 mm/min; ASTM D638
Tensile Strength, Yield	43.1 MPa	6260 psi	5 mm/min; ASTM D638
Elongation at Break	25 %	25 %	5 mm/min; ASTM D638
Tensile Modulus	2.16 GPa	313 ksi	5 mm/min; ASTM D638
Flexural Strength	65.7 MPa	9530 psi	2.8 mm/min; ASTM D790
Flexural Modulus	2.45 GPa	356 ksi	2.8 mm/min; ASTM D790
Izod Impact, Notched	1.37 J/cm @Thickness 6.35 mm	2.57 ft-lb/in @Thickness 0.250 in	ASTM D256
	1.77 J/cm @Thickness 3.17 mm	3.31 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	86.0 Â°C @Thickness 6.40 mm	187 Â°F @Thickness 0.252 in	ASTM D648
Vicat Softening Point	96.0 Â°C	205 Â°F	B/50; ISO R306