Mateck Sodium Chloride (NaCl)
| Category | Ceramic , Halide |
| Manufacturer | Mateck GmbH |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Mateck Sodium Chloride (NaCl).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Optical crystals
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.17 g/cc | 0.0784 lb/in³ | |
| a Lattice Constant | 5.64 Å | 5.64 Å | |
| c Lattice Constant | 5.64 Å | 5.64 Å | |
| Molecular Weight | 58.45 g/mol | 58.45 g/mol |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Vickers Microhardness | 200 | 200 | MPa |
| Hardness, Mohs | 3.0 | 3.0 | |
| Modulus of Elasticity | 32.7 GPa | 4740 ksi | in <111> direction |
| 43.7 GPa | 6340 ksi | in <100> direction | |
| Poissons Ratio | 0.203 | 0.203 | |
| Shear Modulus | 12.8 GPa | 1860 ksi | in <111> direction |
| 15.9 GPa | 2310 ksi | in <100> direction |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 36.4 - 40.8 µm/m-°C @Temperature -60.0 - 60.0 °C |
20.2 - 22.7 µin/in-°F @Temperature -76.0 - 140 °F |
|
| Specific Heat Capacity | 0.871 J/g-°C | 0.208 BTU/lb-°F | |
| Thermal Conductivity | 6.15 W/m-K @Temperature 35.0 °C |
42.7 BTU-in/hr-ft²-°F @Temperature 95.0 °F |
|
| Melting Point | 801 °C | 1470 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.4906 | 1.4906 | n10.6 |
| 1.5467 | 1.5467 | at ne | |
| 1.3822 @Wavelength 20000 nm |
1.3822 @Wavelength 20000 nm |
||
| 1.4947 @Wavelength 10000 nm |
1.4947 @Wavelength 10000 nm |
||
| 1.5153 @Wavelength 6000 nm |
1.5153 @Wavelength 6000 nm |
||
| 1.532 @Wavelength 1000 nm |
1.532 @Wavelength 1000 nm |
||
| 1.7899 @Wavelength 200 nm |
1.7899 @Wavelength 200 nm |
||
| Transmission, Visible | 97 % @Wavelength 500 nm |
97 % @Wavelength 500 nm |
Internal Transmittance |
| IR Transmittance | 5.0 % @Wavelength 20000 nm |
5.0 % @Wavelength 20000 nm |
Internal Transmittance |
| 87 % @Wavelength 15000 nm |
87 % @Wavelength 15000 nm |
Internal Transmittance | |
| UV Transmittance | 16 % @Wavelength 200 nm |
16 % @Wavelength 200 nm |
Internal Transmittance |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cleavability | (100) | perfect |
| Constants of Elastic Compliance (Pa^-1) | 2.285E-11 | S11 |
| -4.69E-12 | S12 | |
| 7.834E-11 | S44 | |
| Symmetry Class | m3m | |
| Syngony | cubic | |
| Thermal Coefficient of Refractive Index | -3.31E-5 to -3.73E-5 | at 3.39 microns for ± 60°C |
| Transmission Range (microns) | 0.2 - 20 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 920 PC (Asia Pacific)
- Karina E 70/236-DA-IS Clear PVC Compound
- Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled
- Borealis Low Sulfur™ LE0594 Crosslinkable Semiconductive Compound for Shielding of Power Cables
- A. Schulman POLYPUR™ FPU 1109 Thermoplastic Polyurethane Compound
- Chevron Phillips MarFlex® D163 Metallocene Linear Low Density Polyethylene, Blown Film
- ELASTO UK Dryflex® 8009-101 Flame Retardant TPE for Injection Molding, Natural
- Chi Mei Polylac® PA-758R ABS - Transparent
- China-Yixing Longly Refractories 99 Alumina Ceramic
- E-Polymers EFLEX® S5060 Extrusion
Copyright © lookpolymers.com All Rights Reserved