Samsung Cheil Industries Starex® HR-0370F ABS, Unreinforced Heat Resistant

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
Manufacturer Samsung, Cheil Industries
Trade Name Starex®
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF Samsung Cheil Industries Starex® HR-0370F ABS, Unreinforced Heat Resistant.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D792
Water Absorption 0.050 %
<br>@Temperature 23.0 °C
 0.050 %
<br>@Temperature 73.4 °F
 ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
<br>@Thickness 3.20 mm
 0.0050 - 0.0070 in/in
<br>@Thickness 0.126 in
 ASTM D955
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
<br>@Thickness 3.20 mm
 0.0060 in/in
<br>@Thickness 0.126 in
 ASTM D955
Melt Flow 0.90 g/10 min
<br>@Load 5.00 kg,<br> Temperature 200 °C
 0.90 g/10 min
<br>@Load 11.0 lb,<br> Temperature 392 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110
110
ASTM D785
Tensile Strength, Yield 46.1 MPa
6680 psi
5 mm/min; ASTM D638
Elongation at Break 14 %
14 %
5 mm/min; ASTM D638
Flexural Strength 68.6 MPa
9950 psi
2.8 mm/min; ASTM D790
Flexural Modulus 2.16 GPa
313 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 1.47 J/cm
<br>@Thickness 6.35 mm
 2.76 ft-lb/in
<br>@Thickness 0.250 in
 ASTM D256
1.57 J/cm
<br>@Thickness 3.17 mm
 2.94 ft-lb/in
<br>@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
<br>@Thickness 6.40 mm
 203 °F
<br>@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 106 °C
223 °F
B/50; ISO R306