Samsung Cheil Industries Starex® HG-0760LT ABS, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® HG-0760LT ABS, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Melt Flow | 5.3 g/10 min @Load 5.00 kg, Temperature 200 °C |
5.3 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength at Break | 39.2 MPa | 5690 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 15 % | 15 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.45 GPa | 356 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 68.6 MPa | 9950 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.45 GPa | 356 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.27 J/cm @Thickness 6.35 mm |
2.39 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.86 J/cm @Thickness 3.17 mm |
3.49 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C @Thickness 6.40 mm |
203 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 6.40 mm |
189 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 99.0 °C | 210 °F | B/50; ISO R306 |
| 101 °C | 214 °F | B/120; ISO R306 |
Users viewing this material also viewed the following:
- Potters Industries Conduct-O-Fil® SG02S40 Silver-coated Sub-10 micron Particles
- Solvay Specialty Polymers Solef® 6012 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
- LyondellBasell Pro-fax 6323 Polypropylene Homopolymer, Easy Molding
- Techmer ES HiFill® PEI TX5 LE
- Polyram PlusTek RA325G5 Nylon 6.6, 25% Glass Fiber, Flame Retardant
- A. Schulman PP 3476 Polypropylene Homopolymer Polypropylene
- Lubrizol ESTANE® ETE55DT3 Ester Based Thermoplastic Polyurethane (European Grade)
- Esstech V-115-1104 Aluminosilicate Glass-Ceramic
- Arlon 55978X030 0.0305" (0.775 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Latrobe LSS™ O1 Tool Steel (ASTM O1)
Copyright © lookpolymers.com All Rights Reserved