| Category | Metal , Ferrous Metal , Austenitic , Stainless Steel , T 300 Series Stainless Steel |
| Manufacturer | AK Steel |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | AK Steel 316L Austenitic Stainless steel.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AK Steel 316L is an extra-low carbon version of AK Steel 316 that minimizes harmful carbide precipitation due to welding.Information provided by AK Steel
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.99 g/cc | 0.289 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell B | 79 | 79 | |
| Tensile Strength, Ultimate | 558 MPa | 80900 psi | |
| Tensile Strength, Yield | 290 MPa @Strain 0.200 % |
42100 psi @Strain 0.200 % |
|
| Elongation at Break | 50 % | 50 % | in 2 inches |
| Modulus of Elasticity | 193 GPa | 28000 ksi | tension |
| Poissons Ratio | 0.25 | 0.25 | Calculated |
| Shear Modulus | 77.0 GPa | 11200 ksi | torsion |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.0 µm/m-°C @Temperature 0.000 - 100 °C |
8.89 µin/in-°F @Temperature 32.0 - 212 °F |
|
| 19.9 µm/m-°C @Temperature <=871 °C |
11.1 µin/in-°F @Temperature <=1600 °F |
||
| Specific Heat Capacity | 0.500 J/g-°C @Temperature 0.000 - 100 °C |
0.120 BTU/lb-°F @Temperature 32.0 - 212 °F |
|
| Thermal Conductivity | 16.2 W/m-K @Temperature 100 °C |
112 BTU-in/hr-ft²-°F @Temperature 212 °F |
|
| 21.4 W/m-K @Temperature 500 °C |
149 BTU-in/hr-ft²-°F @Temperature 932 °F |
||
| Melting Point | 1371 - 1399 °C | 2500 - 2550 °F | |
| Solidus | 1371 °C | 2500 °F | |
| Liquidus | 1399 °C | 2550 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.030 % | <= 0.030 % | |
| Chromium, Cr | 16 - 18 % | 16 - 18 % | |
| Iron, Fe | 62.045 - 72 % | 62.045 - 72 % | As Remainder |
| Manganese, Mn | <= 2.0 % | <= 2.0 % | |
| Molybdenum, Mo | 2.0 - 3.0 % | 2.0 - 3.0 % | |
| Nickel, Ni | 10 - 14 % | 10 - 14 % | |
| Nitrogen, N | <= 0.010 % | <= 0.010 % | |
| Phosphorous, P | <= 0.045 % | <= 0.045 % | |
| Silicon, Si | <= 0.75 % | <= 0.75 % | |
| Sulfur, S | <= 0.030 % | <= 0.030 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000740 ohm-cm | 0.0000740 ohm-cm | |
| Magnetic Permeability | <= 1.02 | <= 1.02 | H = 200 Oersteds, Annealed |
Users viewing this material also viewed the following:
- Osprey Metals HTN 7 Brazing Powder
- Parker Chomerics CHO-BOND® 1121 General Purpose Adhesive-Sealant Silver Silicone
- Total Finaprene® 411x Styrene-Butadiene TPE Copolymer Compounded to 61 Shore A (discontinued **)
- Kleerdex Kydex® L Acrylic/PVC Thermoplastic Sheet (discontinued **)
- Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F)
- SABIC Innovative Plastics LNP LUBRICOMP OCP36 PPS (Asia Pacific)
- Samsung Cheil Industries Starex® VE-0813 ABS, Unreinforced FR
- Williams Advanced Alloys Wambraze™ WB1030 Solder
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 60 PHR N339 Filler
- E-Polymers SEPAZ® LC40 PP Copolymer LFT Resin
Copyright © lookpolymers.com All Rights Reserved