- M. Holland Company MAGMA® LM115-B LLDPE (discontinued **)
M. Holland Company MAGMA® LM115-B LLDPE (discontinued **)
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | M. Holland Company MAGMA® LM115-B LLDPE
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Good Heat Seal, Good Tear Strength, Good ToughnessUses: BlendingProcessing Method: ExtrusionInformation provided by M. Holland.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Thickness | 31.8 microns | 1.25 mil | |
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Elmendorf Tear Strength MD | 260 g | 260 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 490 g | 490 g | ASTM D1922 |
| Dart Drop Test | 830 g | 1.83 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 34.5 MPa | 5000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 27.6 MPa | 4000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 120 °C | 248 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 5.0 % | 5.0 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | <= 149 °C | <= 300 °F | |
| Zone 1 | 149 °C | 300 °F | |
| Melt Temperature | 182 - 232 °C | 360 - 450 °F | |
| Die Opening | 0.0810 - 0.254 cm | 0.0319 - 0.100 in | |
| Blow-up Ratio (BUR) | 1.5 - 3.0 | 1.5 - 3.0 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets |
Users viewing this material also viewed the following:
- Nye Lubricants 757 (RL) Synthetic Oil
- NCMT NanoPAC™ S212 High Performance Polypropylene Nanocomposite
- LTL Color Compounds ColorRxâ„¢ PC-1002ARX Biocompatible Polycarbonate
- Hexcel® HexForce™ 1800 Fiber Glass Fabric
- Aclo Accuguard Polypropylene CP0467V2CSL Copolymer Flame Retardant Copper Stabilized
- Fainplast Compounds KLT 79 Flexible PVC, Insulation Transparent Cables Lead Free
Copyright © lookpolymers.com All Rights Reserved