LATI Latishield 85-08A G/20 PES, Steel/Glass Fibers

Category	Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer	LATI
Trade Name	Latishield
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latishield 85-08A G/20 PES, Steel/Glass Fibers.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

EMI shielding product based on Polyether Sulfone (PES). Steel fibers. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.59 g/cc	0.0574 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0035 - 0.0050 cm/cm	0.0035 - 0.0050 in/in
Linear Mold Shrinkage, Transverse	0.0075 - 0.0090 cm/cm	0.0075 - 0.0090 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	110 MPa	16000 psi
Elongation at Break	2.0 %	2.0 %
Tensile Modulus	7.00 GPa	1020 ksi
Charpy Impact Unnotched	4.50 J/cmÂ²	21.4 ft-lb/inÂ²
Charpy Impact, Notched	0.550 J/cmÂ²	2.62 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	215 Â°C	419 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	205 Â°C	401 Â°F
Vicat Softening Point	210 Â°C @Load 5.00 kg	410 Â°F @Load 11.0 lb
Flammability, UL94	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in
	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in
	V-0 @Thickness 0.750 mm	V-0 @Thickness 0.0295 in

Electrical Properties	Metric	English	Comments
Surface Resistance	7.8 ohm	7.8 ohm

Processing Properties	Metric	English
Melt Temperature	300 - 340 Â°C	572 - 644 Â°F
Mold Temperature	100 - 130 Â°C	212 - 266 Â°F
Drying Temperature	110 - 130 Â°C	230 - 266 Â°F

Descriptive Properties	Value	Comments
Electromagnetic reflection	90 dB
ISO Shrinkage - Pressure	60 MPa