Samsung Cheil Industries Starex® BF-0370 MABS, Unreinforced Scratch Resistant

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Samsung, Cheil Industries
Trade Name Starex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Starex® BF-0370 MABS, Unreinforced Scratch Resistant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Scratch resistant material that is used in the exterior of electric products and household appliancesInformation provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0030 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.0060 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 18 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 18 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 112
112
ASTM D785
Tensile Strength, Yield 51.0 MPa
7400 psi
5 mm/min; ASTM D638
Elongation at Break 25 %
25 %
5 mm/min; ASTM D638
Flexural Strength 75.5 MPa
11000 psi
2.8 mm/min; ASTM D790
Flexural Modulus 2.45 GPa
356 ksi
2.8 mm/min; ASTM D790
Izod Impact, Notched 1.27 J/cm

@Thickness 6.35 mm
 2.39 ft-lb/in

@Thickness 0.250 in
 ASTM D256
1.47 J/cm

@Thickness 3.17 mm
 2.76 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 89.0 °C

@Thickness 6.40 mm
 192 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 102 °C
216 °F
B/50; ISO R306
Flammability, UL94 HB

@Thickness 1.00 - 3.00 mm
 HB

@Thickness 0.0394 - 0.118 in
Descriptive Properties Value Comments
Pencil Hardness HB
1000g, JIS K 5401