POLYMER SEARCH

Wieland Porta Maximum NF PFM Alloy

Category	Metal , Nonferrous Metal , Precious Metal , Gold Alloy
Manufacturer	Wieland
Trade Name	Porta
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Wieland Porta Maximum NF PFM Alloy.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

All-purpose alloy for low-fusing high expanding ceramicsApplications: inlays/onlays, crowns, short span bridges, long span bridges, telescopic and milling works, removable partials, ceramic veneering, acrylic veneeringDental

Physical Properties	Metric	English	Comments
Density	15.4 g/cc	0.556 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Vickers	240	240	HV5/30; after porcelain firing
	260	260	HV5/30; hardened
Tensile Strength, Yield	640.0 MPa @Strain 0.200 %	92820 psi @Strain 0.200 %	after porcelain firing
	700.0 MPa @Strain 0.200 %	101500 psi @Strain 0.200 %	hardened
Elongation at Break	3.0 %	3.0 %	after porcelain firing
	3.0 %	3.0 %	hardened
Modulus of Elasticity	110 GPa	16000 ksi

Thermal Properties	Metric	English	Comments
CTE, linear	16.2 µm/m-°C @Temperature 25.0 - 500 °C	9.00 µin/in-°F @Temperature 77.0 - 932 °F

Component Elements Properties	Metric	English
Gold, Au	71 %	71 %
Indium, In	2.7 %	2.7 %
Iridium, Ir	0.30 %	0.30 %
Palladium, Pd	11 %	11 %
Silver, Ag	13 %	13 %
Zinc, Zn	2.0 %	2.0 %

Processing Properties	Metric	English	Comments
Processing Temperature	799 °C	1470 °F	Preheating Temp.
Melt Temperature	1020 - 1110 °C	1870 - 2030 °F
Casting Temperature	1260 °C	2300 °F

Descriptive Properties	Value	Comments
Color	yellow

Users viewing this material also viewed the following: