Samsung Cheil Industries Infino® XP-2130A PPS
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® XP-2130A PPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.65 g/cc | 1.65 g/cc | ASTM D792 |
| Water Absorption | 0.020 % @Temperature 23.0 °C |
0.020 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.012 cm/cm @Thickness 3.20 mm |
0.0030 - 0.012 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 116 g/10 min @Load 5.00 kg, Temperature 316 °C |
116 g/10 min @Load 11.0 lb, Temperature 601 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 127 MPa | 18500 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 196 MPa | 28400 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 9.81 GPa | 1420 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 0.785 J/cm @Thickness 6.35 mm |
1.47 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C @Thickness 6.40 mm |
518 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm @Temperature 23.0 °C |
1.00e+16 ohm-cm @Temperature 73.4 °F |
50% RH; ASTM D257 |
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dissipation Factor | 0.0020 @Frequency 1.00e+6 Hz |
0.0020 @Frequency 1.00e+6 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- DuPont Nucrel® 2940 Ethylene-Methacrylic Acid Copolymer Resin (discontinued **)
- Kennametal Stellite Stellite® 19
- Metabolix M-veraâ„¢ B5010 Film Grade Compostable Bioplastic
- Ineos N10N-00 Polypropylene Impact Copolymer
- LyondellBasell Astryn EPKT25M Polypropylene Copolymer, Mineral Filled
- Techmer ES HiFill® PA6/6 GF/M15 HS L BK 40/15% Glass/Mineral Fiber Filled
- Samsung Cheil Industries Starex® SF-200H Expandable Polystyrene (EPS) FR
- Diamond Polymers ASA M806 ASA Weatherable Polymers Direct Metallizable Grade, Medium Heat
- Dymax 912 Strain Relief, Wire and Parts Tacking Adhesive
- Arlon R3758R0055 0.065" Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved