Samsung Cheil Industries Infino® WP-1069 PC/ABS, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® WP-1069 PC/ABS, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 47 g/10 min @Load 10.0 kg, Temperature 250 °C |
47 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength at Break | 54.9 MPa | 7960 psi | ASTM D638 |
| Tensile Strength, Yield | 53.0 MPa | 7680 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 87 % | 87 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.01 GPa | 292 ksi | ASTM D638 |
| Flexural Strength | 78.5 MPa | 11400 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 2.21 GPa | 320 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 1.96 J/cm @Thickness 6.35 mm, Temperature -30.0 °C |
3.67 ft-lb/in @Thickness 0.250 in, Temperature -22.0 °F |
ASTM D256 |
| 3.92 J/cm @Thickness 3.17 mm, Temperature -30.0 °C |
7.35 ft-lb/in @Thickness 0.125 in, Temperature -22.0 °F |
ASTM D256 | |
| 4.22 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
7.90 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D256 | |
| 5.69 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
10.7 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 8.20 µm/m-°C @Temperature 40.0 - 100 °C |
4.56 µin/in-°F @Temperature 104 - 212 °F |
ASTM E831 |
| CTE, linear, Transverse to Flow | 8.30 µm/m-°C @Temperature 40.0 - 100 °C |
4.61 µin/in-°F @Temperature 104 - 212 °F |
ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C @Thickness 6.40 mm |
261 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C @Thickness 6.40 mm |
230 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 124 °C | 255 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 6 GF 20 002 PA6 reinforced with glass fiber
- RheTech Products FT2600-677UV Thermoplastic Polyolefin, UV Stabilized, 0848 Black
- I. Stern 870E High Impact Polystyrene Extrusion Grade
- Materion Beryllium Copper Alloy 10C Castings (UNS C82000)
- Momentive Performance Materials Siloprenâ„¢ LSR 2620 Liquid Silicone Rubber - Fast Cure / High Tear
- DuPont™ Nomex® N102 Texturized Filament Yarn
- Eurostar Starpylen MX06023 PP, 20% Milled Glass Fiber Filled, Injection Molded
- CLAL-MSX NICLAFOR® 1000 THX Quenched/Cold Rolled/Precipitation Heat Treated, Rolled Copper Alloy
- ACC EP RSP EPI Engineered Polymers Silicone Polyurea
Copyright © lookpolymers.com All Rights Reserved