SABIC Innovative Plastics LNP THERMOCOMP RC008H PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RC008H PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RC008H is a compound based on Nylon 66 resin containing 40% Carbon Fiber. Added features of this material include: Electrically Conductive, Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.540 % | 0.540 % | 50% RH, 24 hrs; ASTM D570 |
| 0.780 % | 0.780 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 288 MPa | 41800 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 32.0 GPa | 4640 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 429 MPa | 62200 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 26.1 GPa | 3790 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 1.08 J/cm | 2.02 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 12.19 J/cm | 22.84 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 71.0 kJ/m² | 33.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 15.0 J @Temperature 23.0 °C |
11.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 49.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
27.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 7.24 µm/m-°C @Temperature -30.0 - 30.0 °C |
4.02 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 261 °C | 502 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 255 °C @Thickness 3.20 mm |
491 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE G 7155 BLK
- Polymer Resources TP-HG15 Polybutylene Terephthalate, 15% Glass Reinforced Alloy
- LG Chemical Lupoy 1200-15 Polycarbonate Resin
- Solvay Specialty Polymers Udel® GF-120 Polysulfone (PSU), Glass Fiber
- SABIC Innovative Plastics LNP THERMOCOMP WX05502 Polyester Elastomer
- UBE 7034MT2 Nylon 6/12 Monofilament (Drawing Ratio=5.5)
- DuPont Performance Polymers Hytrel® 4556 Polyester Elastomer TPC-ET (Unverified Data**)
- Diamond Polymers ABS 3500 ELG Natural 1003 Injection Molding Grade, High Flow, Medium Impact, Low Gloss
- Entec Hypro™ PPH-GF40 Natural Homopolymer Polypropylene, 40% Glass Reinforced
- Addiplast Addinyl B2 Nylon 6
Copyright © lookpolymers.com All Rights Reserved