Samsung Cheil Industries Infino® TN-1200 PC, Unreinforced FR
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® TN-1200 PC, Unreinforced FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 60 g/10 min @Load 10.0 kg, Temperature 250 °C |
60 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength, Yield | 68.6 MPa | 9960 psi | 50 mm/min; ASTM D638 |
| Flexural Strength | 108 MPa | 15700 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.441 J/cm @Thickness 3.17 mm |
0.827 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C @Thickness 6.40 mm |
203 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 108 °C | 226 °F | B/50; ISO R306 |
| Flammability, UL94 | V-0 @Thickness 2.00 mm |
V-0 @Thickness 0.0787 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 0.60 % @Thickness 3.20 mm |
0.60 % @Thickness 0.126 in |
ASTM D1003 |
| Transmission, Visible | 89 % @Thickness 3.20 mm |
89 % @Thickness 0.126 in |
ASTM D1003 |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Hytrel® 4069 TPC-ET (Unverified Data**)
- SABIC Innovative Plastics LNP LUBRICOMP DFL23 PC
- LG Chemical Lupoy NF1005F 03R Polycarbonate Resin
- SK Chemicals SKYTHANE® 155D S series Polyurethane
- Teknor Apex Monprene® MP-1823 AS Thermoplastic Elastomer
- DSM Akulon® F150-CZ PA6
- Eagle Brass 102 OF COPPER (Non-Certified), Hard
- Fainplast Compounds PM 55 Flexible PVC, Lead Free
- Arkema Group Rilsan® 6733 Nylon 11, Flexible Tubing Grade (Conditioned)
- Fainplast Compounds MPH 78/T Medical Flexible PVC, Extrusion
Copyright © lookpolymers.com All Rights Reserved