- SABIC Innovative Plastics Lexan® HFD1810 PC Copolymer
SABIC Innovative Plastics Lexan® HFD1810 PC Copolymer
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® HFD1810 PC Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
40 MFR LEXAN High Flow Ductile Copolymer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 40 g/10 min @Load 1.20 kg, Temperature 300 °C |
40 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 38 g/10 min @Load 1.20 kg, Temperature 300 °C |
38 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 56.0 MPa | 8120 psi | Type I, 50 mm/min; ASTM D638 |
| 56.0 MPa | 8120 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D638 |
| 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 97 % | 97 % | 50 mm/min; ISO 527 |
| 130 % | 130 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 5.5 % | 5.5 % | Type I, 50 mm/min; ASTM D638 |
| 6.0 % | 6.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.18 GPa | 316 ksi | 1 mm/min; ISO 527 |
| 2.27 GPa | 329 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 91.0 MPa | 13200 psi | 2 mm/min; ISO 178 |
| 100 MPa | 14500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.18 GPa | 316 ksi | 2 mm/min; ISO 178 |
| 2.24 GPa | 325 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 7.28 J/cm | 13.6 ft-lb/in | ASTM D256 |
| 1.10 J/cm @Temperature -30.0 °C |
2.06 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 6.99 J/cm @Temperature 0.000 °C |
13.1 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 58.0 kJ/m² | 27.6 ft-lb/in² | 80*10*3; ISO 180/1A |
| 11.0 kJ/m² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB | NB | Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 6.40 J/cm² | 30.5 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 56.0 J @Temperature 23.0 °C |
41.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 95.0 J | 70.1 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C @Thickness 3.20 mm |
250 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 110 °C @Thickness 3.20 mm |
230 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 129 °C | 264 °F | Rate B/50; ISO 306 |
| 130 °C | 266 °F | Rate B/120; ISO 306 | |
| 135 °C | 275 °F | Rate B/50; ASTM D1525 | |
| UL RTI, Electrical | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 0.300 mm |
HB @Thickness 0.0118 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.582 | 1.582 | ASTM D542 |
| Haze | <= 1.0 % @Thickness 2.54 mm |
<= 1.0 % @Thickness 0.100 in |
ASTM D1003 |
| Transmission, Visible | 88 % | 88 % | 2.54 mm; ASTM D1003 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASS | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Pyrotek TS-114 Thermoset Electrical Insulation Product (Nema Grade: GPO-3)
- Radici Radilon® A HSX (dry) Nylon 66
- Ravago Manufacturing Americas Hysun™ A6020 ASA+PC
- SABIC BC 111 Crystalline Polyethylene Terephthalate
- KKPC Kuhmo GP 125EI General Purpose GPPS
- Haynes Hastelloy® C-22® alloy, GTAW, aged 4000 hours at 450°C (800°F), notched
- Spartech PETG 3D Lenticular 3-D Specialty Sheet
- Uniseal BETABRACE™ 85002 Epoxy
- A. Schulman POLYFORT™ PX 1042
- Polyram RamTal PM340S6 Polyacetal for Injection Molding, 30% Glass-Beads Filled
Copyright © lookpolymers.com All Rights Reserved