SYNTHOS Forsan® 846 Acrylonitrile Butadiene Styrene (ABS)

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SYNTHOS Kralupy a.s.
Trade Name Forsan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SYNTHOS Forsan® 846 Acrylonitrile Butadiene Styrene (ABS).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High impact, medium flow, glossy, suitableApplications: General purpose, transport packaging, furniture, leisure time equipmentContainers, suitcases, profiles, ABS sheets, skis, helmets, garden equipment, etc.Synthos was formerly known as Kaucuk. All information provided by Synthos.
Physical Properties Metric English Comments
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
Internal; 50x50mm
Melt Flow 7.35 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 7.35 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 Granulate; ISO 1133/U
Mechanical Properties Metric English Comments
Ball Indentation Hardness 74.0 MPa
10700 psi
H 358/30; Ø 50x4mm; ISO 2039-1
Tensile Strength at Break 27.0 MPa

@Temperature 23.0 °C
 3920 psi

@Temperature 73.4 °F
 50mm/min; ISO 527-2/1A/50
Tensile Strength, Yield 36.0 MPa

@Temperature 23.0 °C
 5220 psi

@Temperature 73.4 °F
 50mm/min; ISO 527-2/1A/50
Elongation at Break 9.0 %
9.0 %
50mm/min; ISO 527-2/1A/50
Tensile Modulus 1.90 GPa

@Temperature 23.0 °C
 276 ksi

@Temperature 73.4 °F
 1mm/min; ISO 527-2/1A/1
Flexural Strength 50.0 MPa

@Temperature 23.0 °C
 7250 psi

@Temperature 73.4 °F
 2mm/min; 80x10x4mm; ISO 178
Flexural Modulus 1.70 GPa

@Temperature 23.0 °C
 247 ksi

@Temperature 73.4 °F
 2mm/min; 80x10x4mm; ISO 178
Izod Impact, Notched (ISO) 33.0 kJ/m²

@Temperature 23.0 °C
 15.7 ft-lb/in²

@Temperature 73.4 °F
 80x10x4mm, r=0.25; V-notch; ISO 180/1A
Charpy Impact Unnotched 19.0 J/cm²

@Temperature 23.0 °C
 90.4 ft-lb/in²

@Temperature 73.4 °F
 80x10x4mm; ISO 179/1eU
Charpy Impact, Notched 3.00 J/cm²

@Temperature 23.0 °C
 14.3 ft-lb/in²

@Temperature 73.4 °F
 80x10x4mm, r=0.25; V-notch; ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 96.0 °C
205 °F
80x10x4mm; ISO 75-2/Af
Vicat Softening Point 91.0 °C
196 °F
50°C/h; 50N; 10x10x4mm; ISO 306/B50
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
 Tested in EZÚ Praha
Glow Wire Test 650 °C
1200 °F
Ø 93x3mm; IEC 60695-2-1
Electrical Properties Metric English Comments
Volume Resistivity 6.00e+16 ohm-cm
6.00e+16 ohm-cm
500V; Ø 93x3mm; IEC 60093
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
500V; Ø 93x3mm; IEC 60093
Dielectric Constant 2.6

@Frequency 1e+6 Hz
 2.6

@Frequency 1e+6 Hz
 Ø 50x3mm; IEC 60250
<= 2.7

@Frequency 50 Hz
 <= 2.7

@Frequency 50 Hz
 Ø 50x3mm; IEC 60250
Dielectric Strength 13.0 kV/mm

@Thickness 3.00 mm
 330 kV/in

@Thickness 0.118 in
 Transformer Oil; IEC 60243-1
58.0 kV/mm

@Thickness 0.500 mm
 1470 kV/in

@Thickness 0.0197 in
 Transformer Oil; IEC 60243-1
Dissipation Factor 0.0040

@Frequency 50 Hz
 0.0040

@Frequency 50 Hz
 Ø 93x3mm; IEC 60250
0.0070

@Frequency 1e+6 Hz
 0.0070

@Frequency 1e+6 Hz
 Ø 93x3mm; IEC 60250
Arc Resistance 73 sec
73 sec
Ø 93x3mm; IEC 61621
Comparative Tracking Index 400 V
400 V
Solution A; Ø 93x3mm; IEC 60112