SIDPEC EGYPTENE® LL 0209 AA LLDPE Film
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | SIDPEC (Sidi Kerir Petrochemicals Co.) |
| Trade Name | EGYPTENE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SIDPEC EGYPTENE® LL 0209 AA LLDPE Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications:Heavy duty sacksAgricultural films and linersProduce bags, stretch filmFilm properties were measured on 15 micron film extruded at a blow up ratio of 2:1.Information provided by Interchim s.r.l., official distributor of Sidi Kerir Petrochemicals Co. (SIDPEC) Products
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ISO 1872/1 |
| Thickness | 15.0 microns | 0.591 mil | |
| Melt Flow | 0.90 g/10 min @Load 2.16 kg |
0.90 g/10 min @Load 4.76 lb |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ISO 1184 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ISO 1184 |
| Film Elongation at Break, MD | 620 % | 620 % | ISO 1184 |
| Film Elongation at Break, TD | 840 % | 840 % | ISO 1184 |
| Elmendorf Tear Strength, MD | 5.71 g/micron | 145 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 14.6 g/micron | 370 g/mil | ASTM D1922 |
| Dart Drop | 10.0 g/micron | 254 g/mil | Calculated from thickness |
| Dart Drop Test | 150 g | 0.331 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 41.0 MPa | 5950 psi | ISO 1184 |
| Film Tensile Strength at Break, TD | 32.0 MPa | 4640 psi | ISO 1184 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 225 °C | 437 °F |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-FOIL CCH Shielding Tape
- 3M Dyneon™ Fluorel™ FE-5840Q Fluoroelastomer VF2 + HFP + TFE Terpolymer (discontinued **)
- Polymer Resources NY66-G13-[color]-H Nylon 66, 13% Glass Reinforced, Heat Stabilized
- LyondellBasell Petrothene® NA345196 Low Density Polyethylene (Film Extrusion)
- Fujipoly Industries Zebra® 2005 Carbon Solid Self-Supported Connectors
- Indium Corp. Indalloy 56 Bismuth Solder Alloy
- Lubrizol Estane® CR180A Thermoplastic Polyurethane
- Dow DNDA-8335 NT 7 Linear Low Density Polyethylene Resin
- Elgiloy® Co-Cr-Ni Alloy, Wire, 40% Cold Reduction, Heat Treated
- Addiplast Addinyl C2 R Nylon 66/6
Copyright © lookpolymers.com All Rights Reserved