Oxford Polymers PC 68 Unfilled Polycarbonate for Injection and Extrusion Molding
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Oxford Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Oxford Polymers PC 68 Unfilled Polycarbonate for Injection and Extrusion Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unfilled Polycarbonate for Injection and Extrusion MoldingInformation provided by Oxford Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Melt Flow | 7.0 g/10 min | 7.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.5 MPa | 9500 psi | ASTM D638 |
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ASTM D638 |
| Elongation at Break | 125 % | 125 % | ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | ASTM D638 |
| Tensile Modulus | 2.38 GPa | 345 ksi | ASTM D638 |
| Flexural Strength | 97.9 MPa | 14200 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | ASTM D790 |
| Compressive Strength | 86.2 MPa | 12500 psi | ASTM D695 |
| Izod Impact, Notched | 8.01 J/cm @Temperature 23.0 °C |
15.0 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | ASTM D648 |
| Flammability, UL94 | V-2 | V-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 282 °C | 540 °F |
Users viewing this material also viewed the following:
- Nyco NYAD® 325 Wollastonite
- Parker Chomerics CHO-BOND 1026 Conductive Silicone Splicing Compound
- Solvay Specialty Polymers Halar® 300DA Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)
- Sibur H030 GP/1 Polypropylene Homopolymer
- Sax Polymers SAXALEN PPH335T20 Polypropylene Homopolymer, 20% Talc Filled
- Teknor Apex Uniprene® UN-1069A Thermoplastic Elastomer
- DSM Akulon® F126-C Nylon 6 (European Grade) (Dry)
- Dow AMPLIFY™ EA 101 Ethylene-ethyl Acrylate (EEA)
- 3M CN-3190 EMI Shielding Tape
Copyright © lookpolymers.com All Rights Reserved