- Performance Polymers IPS II PPL-C4150 PEKK (Polyetherketoneketone) Linear 30 % Glass Fiber Reinforced Molding Grade
Performance Polymers IPS II PPL-C4150 PEKK (Polyetherketoneketone) Linear 30 % Glass Fiber Reinforced Molding Grade
| Category | Polymer , Thermoplastic , Polyketone , PEKK, Reinforced |
| Manufacturer | Performance Polymers |
| Trade Name | IPS II |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Performance Polymers IPS II PPL-C4150 PEKK (Polyetherketoneketone) Linear 30 % Glass Fiber Reinforced Molding Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Amber pelletsInformation provided by Infinite Polymer System II.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| Water Absorption | 0.040 % | 0.040 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 103 | 103 | ASTM D785 |
| Tensile Strength at Break | 186 MPa | 27000 psi | ASTM D638 |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| Modulus of Elasticity | 12.4 GPa | 1800 ksi | ASTM D638 |
| Flexural Yield Strength | 255 MPa | 37000 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Compressive Yield Strength | 220 MPa | 31900 psi | ASTM D695 |
| Shear Strength | 220 MPa | 31900 psi | ASTM D732 |
| Izod Impact, Notched | 0.940 J/cm @Thickness 3.17 mm |
1.76 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.0 µm/m-°C | 8.89 µin/in-°F | Below glass transition temp; ASTM D696 |
| Thermal Conductivity | 0.440 W/m-K | 3.05 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 360 °C | 680 °F | DSC |
| Deflection Temperature at 1.8 MPa (264 psi) | 321 °C | 610 °F | ASTM D648 |
| Glass Transition Temp, Tg | 160 °C | 320 °F | DSC |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | 2.00e+16 ohm | 2.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.3 @Frequency 1000 Hz |
3.3 @Frequency 1000 Hz |
ASTM D150 |
| Dielectric Strength | 23.6 kV/mm | 599 kV/in | ASTM D149 |
| Dissipation Factor | 0.0040 @Frequency 1000 Hz |
0.0040 @Frequency 1000 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- PolyOne Lubri-Tech™ AT-10CF/15T-2S Acetal-Copolymer, Carbon Fiber Reinforced, PTFE/Silicone Lubricated (disco
- Henkel Hysol EA 9896 WPP Peel Ply
- Covestro Makrolon® 2405 MAS048 Polycarbonate
- Dow AFFINITY™ EG 8185 Polyolefin Plastomer (POP)
- Fainplast Compounds GA 89/3 Flexible PVC, Flame Retardant Sheathing
- Fainplast Compounds GS 7216 Flexible PVC, Injection Molding for Footwear
- 3M 7603 Clear Vinyl Label Material
- Arlon 55106R030 0.030" (0.762 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Solvay RHODAFAC® RE-610 E Surfactant
- Karina E 06/30-FC-HSF MBU Blue (OP) Color Concentrate
Copyright © lookpolymers.com All Rights Reserved