- SABIC Innovative Plastics Xenoy® 6620U PBT+PC
SABIC Innovative Plastics Xenoy® 6620U PBT+PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® 6620U PBT+PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT+PC, Unfilled, Impact Modified, UV stabilized. Outstanding low temperature impact performance and chemical resistance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.14 % | 0.14 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.016 - 0.018 cm/cm @Thickness 3.20 mm |
0.016 - 0.018 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.016 - 0.018 cm/cm @Thickness 3.20 mm |
0.016 - 0.018 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 21.9 g/10 min @Load 5.00 kg, Temperature 266 °C |
21.9 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 |
| Melt Index of Compound | 17 g/10 min @Load 5.00 kg, Temperature 265 °C |
17 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 31.0 MPa | 4500 psi | 50 mm/min; ISO 527 |
| 32.0 MPa | 4640 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 |
| 43.0 MPa | 6240 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 19.4 % | 19.4 % | 50 mm/min; ISO 527 |
| 145 % | 145 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 3.9 % | 3.9 % | 50 mm/min; ISO 527 |
| 4.2 % | 4.2 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 1.78 GPa | 258 ksi | 50 mm/min; ASTM D638 |
| 1.83 GPa | 265 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 60.0 MPa | 8700 psi | 2 mm/min; ISO 178 |
| 63.0 MPa | 9140 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 1.69 GPa | 245 ksi | 2 mm/min; ISO 178 |
| 1.78 GPa | 258 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 8.97 J/cm | 16.8 ft-lb/in | ASTM D256 |
| 6.67 J/cm @Temperature -30.0 °C |
12.5 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 16.02 J/cm | 30.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 54.0 kJ/m² | 25.7 ft-lb/in² | 80*10*4; ISO 180/1A |
| 51.0 kJ/m² @Temperature -30.0 °C |
24.3 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 7.20 J/cm² | 34.3 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 56.0 J @Temperature 23.0 °C |
41.3 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 98.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
54.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 98.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
54.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 105 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 105 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C @Thickness 6.40 mm |
208 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 60.0 °C @Thickness 6.40 mm |
140 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 118 °C | 244 °F | Rate B/50; ISO 306 |
| 121 °C | 250 °F | Rate B/120; ISO 306 | |
| 123 °C | 253 °F | Rate B/50; ASTM D1525 | |
| UL RTI, Electrical | 75.0 °C | 167 °F | UL 746B |
| UL RTI, Mechanical with Impact | 75.0 °C | 167 °F | UL 746B |
| UL RTI, Mechanical without Impact | 75.0 °C | 167 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 120 - 180 sec | 120 - 180 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | UL 746A |
| Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 10.0 - 25.4 mm/min | 0.394 - 1.00 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Specific Volume | 0.83cm^3/g | ASTM D792 |
Users viewing this material also viewed the following:
- Omni Plastics OmniLon™ 6/6 PA6/6 HSL Unfilled/ Impact Modified Nylon
- Abatron 810326 A/B Filled Potting Compound (discontinued **)
- PSM Industries Pacific Sintered Metals Yellow Brass BZ-111-U Powdered Metal
- Indium Corp. Indalloy 44 Bismuth Solder Alloy
- Saint-Gobain Meldin® 7022 Isostatically Molded Graphite Filled Polyimide
- ChevronTexaco 68 AW Hydraulic Oil
- Buckeye Polymers BP FLEX D5512 RU BLK Thermoplastic Polyolefin
- C.O.I.M. LARIPUR® LPR9060EF PTMG Polyether Polyurethane
- 3A Composites Core Materials AIREX® R82.110 High Performance Structural Foam
Copyright © lookpolymers.com All Rights Reserved