SABIC Innovative Plastics Xenoy® 1731A PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® 1731A PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT+PC, Good Impact , Excellent physical property retention in automotive exteriors and OVAD.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D 792 |
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.080 % | 0.080 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.28 % @Temperature 23.0 °C |
0.28 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0065 - 0.0073 cm/cm @Thickness 3.20 mm |
0.0065 - 0.0073 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.0 g/10 min @Load 5.00 kg, Temperature 250 °C |
8.0 g/10 min @Load 11.0 lb, Temperature 482 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 9.6 g/10 min @Load 5.00 kg, Temperature 250 °C |
9.6 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 57.0 MPa | 8270 psi | 50 mm/min; ISO 527 |
| 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D 638 |
| 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 104 % | 104 % | 50 mm/min; ISO 527 |
| 108 % | 108 % | Type I, 50 mm/min; ASTM D 638 | |
| 240 % | 240 % | Type I, 10 mm/min; SABIC - Japan Method | |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| 5.6 % | 5.6 % | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Modulus | 2.37 GPa | 344 ksi | 5 mm/min; ASTM D 638 |
| 2.37 GPa | 344 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
| 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.12 GPa | 307 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 2.21 GPa | 321 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.76 J/cm @Temperature -30.0 °C |
3.30 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 8.14 J/cm @Temperature 23.0 °C |
15.2 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| 1.60 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
3.00 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² @Temperature -30.0 °C |
7.61 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 59.0 kJ/m² @Temperature 23.0 °C |
28.1 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.30 J/cm² @Temperature -30.0 °C |
6.19 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 6.50 J/cm² @Temperature 23.0 °C |
30.9 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Impact Test | 58.0 J @Temperature 23.0 °C |
42.8 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 83.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 83.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 83.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 83.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
46.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 241 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 110 °C @Thickness 3.20 mm |
230 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| 120 °C @Thickness 6.40 mm |
248 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C | 208 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 92.0 °C @Thickness 3.20 mm |
198 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| 105 °C @Thickness 6.40 mm |
221 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 130 °C | 266 °F | Rate B/50; ASTM D 1525 |
| 130 °C | 266 °F | Rate B/50; ISO 306 | |
| 131 °C | 268 °F | Rate B/120; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASS | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- MV Labs I860 H5IO6 Periodic acid
- SABIC Innovative Plastics Lexan® 161R PC (Europe-Africa-Middle East)
- Kazanorgsintez PE80B-285D High Density Polyethylene Composite, Film Grade
- Lucite International Perspexâ„¢ XT IM60 Acrylic Impact Modified Extruded Sheet
- ExxonMobil Mobilgrease HTR
- CMW® ELKONITE® 10W3 Copper Tungsten RWMA Class 11
- AFE Technologies Cronite 34Ni/25Cr/Nb No. HR 33 Nb
- 3M FL01100N Lexan Label Product
- BASF Ultramid® 8333G HI HS BK-102 33% Glass Filled PA6 (Dry)
- Samyang Triloy® S460G15 Polymer Alloy, Reinforced
Copyright © lookpolymers.com All Rights Reserved