SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xylex |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC+ POLYESTER unreinforced alloy developed for optical or lense market. Chemical resistance.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.120 % | 0.120 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 265 °C |
21 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| 44 g/10 min @Load 1.20 kg, Temperature 300 °C |
44 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 | |
| Melt Index of Compound | 20 g/10 min @Load 2.16 kg, Temperature 265 °C |
20 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 42 g/10 min @Load 1.20 kg, Temperature 300 °C |
42 g/10 min @Load 2.65 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 52.0 MPa | 7540 psi | Type I, 50 mm/min; ASTM D638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
| 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 150 % | 150 % | Type I, 50 mm/min; ASTM D638 |
| >= 150 % | >= 150 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | Type I, 50 mm/min; ASTM D638 |
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 1.84 GPa | 267 ksi | 50 mm/min; ASTM D638 |
| 1.90 GPa | 276 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 83.0 MPa | 12000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.94 GPa | 281 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 6.60 J/cm | 12.4 ft-lb/in | ASTM D256 |
| 0.560 J/cm @Temperature -30.0 °C |
1.05 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| 5.00 kJ/m² @Temperature -10.0 °C |
2.38 ft-lb/in² @Temperature 14.0 °F |
80*10*4; ISO 180/1A | |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 95.0 J @Temperature 23.0 °C |
70.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 85.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| 115 µm/m-°C @Temperature -40.0 - 40.0 °C |
63.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 85.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
47.2 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| 105 µm/m-°C @Temperature -40.0 - 40.0 °C |
58.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C @Thickness 3.20 mm |
216 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 92.0 °C | 198 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | |
| 88.0 °C @Thickness 3.20 mm |
190 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 106 °C | 223 °F | Rate B/120; ISO 306 |
| 107 °C | 225 °F | Rate B/50; ISO 306 | |
| 108 °C | 226 °F | Rate B/50; ASTM D1525 | |
| Flammability, UL94 | V-2 @Thickness 3.00 mm |
V-2 @Thickness 0.118 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.0 % @Thickness 2.54 mm |
2.0 % @Thickness 0.100 in |
ASTM D1003 |
| Transmission, Visible | 88 % | 88 % | 2.54 mm; ASTM D1003 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable JG513G2 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Petroquimica Triunfo Trithene® TS 7045 LDPE - Film - Plastification
- Samsung Cheil Industries Starex® LX-0935 S ABS, Unreinforced Metallic-Look
- Zig Sheng Industrial ZISAMIDE® TP4208 Nylon 6
- Zeon Chemicals Nipol® 1094-80 Nitrile Elastomer
- DayGlo ZQ Pigments ZQ-21 Corona Magenta
- Ametek High Purity Nickel Strip 899E Annealed
- ExxonMobil Escorene® HD-7000F HMW-HDPE Blown Film Resin (discontinued **)
- Kazanorgsintez 153-16 Composition of Low Density Polyethylene, Crack-Proof
Copyright © lookpolymers.com All Rights Reserved