SABIC Innovative Plastics Valox® IQ3001 PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® IQ3001 PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Valox IQ3001 is an unfilled environmentally responsible iQ-PBT resin modified with elastomer. Targeted for flexible hinge applications.
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
ASTM D792
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Moisture Absorption 0.0700 %
0.0700 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.11 %
0.11 %
ISO 62
Linear Mold Shrinkage, Flow 0.021 - 0.027 cm/cm

@Thickness 3.20 mm
 0.021 - 0.027 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.021 - 0.027 cm/cm

@Thickness 3.20 mm
 0.021 - 0.027 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 26 g/10 min

@Load 1.20 kg,
Temperature 250 °C
 26 g/10 min

@Load 2.65 lb,
Temperature 482 °F
 ASTM D1238
Melt Index of Compound 24 g/10 min

@Load 1.20 kg,
Temperature 250 °C
 24 g/10 min

@Load 2.65 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
50 mm/min; ISO 527
51.0 MPa
7400 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 55.0 MPa
7980 psi
50 mm/min; ISO 527
56.0 MPa
8120 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 60 %
60 %
Type I, 50 mm/min; ASTM D638
60 %
60 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
Type I, 50 mm/min; ASTM D638
5.0 %
5.0 %
50 mm/min; ISO 527
Tensile Modulus 2.60 GPa
377 ksi
5 mm/min; ASTM D638
2.60 GPa
377 ksi
1 mm/min; ISO 527
Flexural Yield Strength 80.0 MPa
11600 psi
2 mm/min; ISO 178
82.0 MPa
11900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.40 GPa
348 ksi
2 mm/min; ISO 178
2.50 GPa
363 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.280 J/cm
0.525 ft-lb/in
ASTM D256
0.270 J/cm

@Temperature -30.0 °C
 0.506 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Unnotched 17.0 J/cm
31.8 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
4.00 kJ/m²

@Temperature -30.0 °C
 1.90 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Charpy Impact, Notched 1.10 J/cm²
5.23 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 23.0 J

@Temperature 23.0 °C
 17.0 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 85.0 µm/m-°C

@Temperature -40.0 - 150 °C
 47.2 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
85.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
 47.2 µin/in-°F

@Temperature -22.0 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 79.0 µm/m-°C

@Temperature -40.0 - 150 °C
 43.9 µin/in-°F

@Temperature -40.0 - 302 °F
 ASTM E 831
79.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
 43.9 µin/in-°F

@Temperature -22.0 - 176 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 135 °C
275 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
148 °C

@Thickness 6.40 mm
 298 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 48.0 °C
118 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
54.0 °C

@Thickness 3.20 mm
 129 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 177 °C
351 °F
Rate B/50; ASTM D1525
177 °C
351 °F
Rate B/120; ISO 306
178 °C
352 °F
Rate B/50; ISO 306